軸受鋼の応力漸減回転曲げ疲労試験におけるFGA形成機構
スポンサーリンク
概要
- 論文の詳細を見る
In order to examine the fine granular area (FGA) formed timing in under rotating bending fatigue for high strength steel, the rotating bending tests were carried out under decremental step loads for high carbon chromium bearing steel. The decremental step loads were three conditions, the ratio of cumulative number of stress cycles at the high stress level were 2, 4, 7% against the average of the fatigue life in the interior inclusion induced fracture, and were 80% against the average of the fatigue life in the surface induced fracture. From the experimental results, FGA was observed around the inclusion at the fracture surface of the interior induced fracture specimens. The size of FGA and the stress intensity factor range of FGA were almost similar to each other for every condition.
著者
関連論文
- アルミニウム合金の長寿命疲労挙動に対するアルマイト処理および微細組織の影響(M&M2009材料力学カンファレンス)
- 1150 プラスチック製短下肢装具の疲労試験及び信頼性評価に関する研究(G03-4 材料力学(4)複合材料2,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 金属材料の疲労試験データに対する標準的S-N曲線回帰法の提案(信頼性工学)
- 時間強度分布に基づく疲労データ解析モデルの提案
- 233 金属材料疲労データに対する S-N 曲線回帰法 : 材料学会標準に向けて
- 231 統計的疲労試験におけるステアケース法の推定精度の検討
- 欠陥分布を考慮した金属材料の疲労寿命分布に関する理論的考察
- 604 プラスチック製短下肢装具疲労試験機の開発及び基礎実験(生体・医療材料-I,生体・医療材料,オーガナイスドセッション12,第53期学術講演会)
- アルミニウム合金の長寿命疲労挙動に対するアルマイト処理および微細組織の影響
- 112 日本材料学会標準S-N曲線回帰法による鉄鋼材料の疲労特性の検討(鉄鋼材料の疲労強度特性,疲労の機構と強度信頼性,オーガナイスドセッション1,第53期学術講演会)