735 高炭素クロム軸受鋼の長寿命軸荷重疲労特性の応力比依存性に関する研究

概要

論文の詳細を見る
Effect of stress ratio on fatigue properties of a bearing steel including long life region was experimentally examined under axial loading. As a result, the complicated S-N property was well explained as duplex S-N characteristics obtained by superposition of S-N curves for surface induced fracture and interior inclusion induced fracture irrespective of stress ratio. Fish-eye marks were necessarily observed on the fracture surfaces failed in the latter fracture mode and an inclusion was found at the center of the fish-eye. It was finally found that the fatigue fracture of this steel in the long life region occurred through three different processes of (1) formation of the characteristic area of FGA, (2) crack propagation to form the fish-eye and (3) rapid crack propagation to cause the catastrophic fracture.
社団法人日本機械学会の論文
2003-08-05