水溶液中のアルギン酸分子におけるマンヌロン酸及びグルロン酸残基当りの分子鎖長

スポンサーリンク

概要

• 論文の詳細を見る

• Limiting viscosity number was measured for two alginate samples with different mannuronate (M)/guluronate (G) ratios in dilute aqueous salt solutions. Root mean square end-to-end distance <γ<SUP>2</SUP>><SUP>1/2</SUP> obtained was ca. 600Å for the M rich sample (M/G=1.85) having a viscosity average molecular weight M<SUB>V</SUB> of 6.66×10<SUP>4</SUP> and ca. 480Å for the G rich sample (M/G=0.55) with M<SUB>V</SUB>=2.82×10<SUP>4</SUP>. The contribution from the M and G components to <γ<SUP>2</SUP>> was estimated and the molecular length defined by <γ<SUB>M</SUB><SUP>2</SUP>>/P<SUB>M</SUB> and <γ<SUB>G</SUB><SUP>2</SUP>>/P<SUB>G</SUB> for the M and G residues, (i. e., the mean-square end-to-end distance per monomeric unit for each component) were estimated. Here <γ<SUB>M</SUB><SUP>2</SUP>>, <γ<SUB>G</SUB><SUP>2</SUP>> and P<SUB>M</SUB>, P<SUB>G</SUB> are mean-square end-to-end distances and degree of polymerization which are assigned to the M and G components in an alginate chain, respectively. The present investigation has revealed that the molecular extension of the G component is larger than that of the M component, and that the <γ<SUB>G</SUB><SUP>2</SUP>>/P<SUB>G</SUB> value is ca. 2.2 times as large as the <γ<SUB>M</SUB><SUP>2</SUP>>/P<SUB>M</SUB> value.

• 特定非営利活動法人 日本バイオレオロジー学会の論文

著者

• 松本 孝芳

  京都大学工学部

• 川井 正弘

  京都大学生体医療工学研究センター

• 松本 孝芳

  京都大学工学部高分子化学教室

• 中島 章夫

  大阪工業大学工学部応用化学教室

• 升田利 史郎

  京都大学生体医療工学研究センター

関連論文

• 分散系にみられる非線形粘弾性の解析法
• 高分子ー粒子混合系の粘弾性
• 数種の懸濁液の流動特性
• ポリスチレン溶液-球形粒子分散系の長いタイムスケールにおけるレオロジー的性質
• ポリエチレン溶液-ラテックス分散系の非線形粘弾性
• 小角X線散乱による親水性微小コロイド粒子の表面構造の定量的解析
• ポリスチレン溶液-ラテックス分散系のレオロジー的性質
• カルボキシメチルキチン水溶液のゲル化に及ぼす三価金属陽イオン種の影響
• アルギン酸ゲルのレオロジー的性質
• 二価金属イオンによるアルギン酸水溶液のゲル化に及ぼす添加塩種の影響
• アルギン酸水溶液のMg^イオンによるゲル化に及ぼすマンヌロン酸/グルロン酸比の影響
• 分散系にみられる非線形粘弾性 (レオロジー(特集))
• 水溶液中のアルギン酸分子におけるマンヌロン酸及びグルロン酸残基当りの分子鎖長

もっと見る 閉じる

スポンサーリンク