生分解可能澱粉添加プラスチックの土壌埋設による評価研究-2-劣化メカニズム解析
スポンサーリンク
概要
- 論文の詳細を見る
Continued from a previous report, the evaluation of lay-in-soil test defined treatment condition carried out for eight months for the biodegradable plastics, LDPE, L-LDPE, HDPE, added starch and other additives. As a result, a lowering of physical property and a little of weight loss were recognized on samples treated in high bioorganismic activity soil. In addition, it was recognized that the added starch and oil reduced and the oil accelerated the degradation of polymer at lay-in-soil treatment. The starch was not directly concerned to polymer degradation, but with oil it accerelated polymer degradation. As a result, increasing of carbonyl groups, lowering of oxidation initiation temperature, change of melting point and so on were observed. At the vigorous degradation parts around the void which was the result of polymer lost, element O suggesting oxidation, S, Fe, Al and S were observed concentrically by surface analysis using EPMA.
- 日本ゴム協会の論文
著者
-
大武 義人
化学品検査協会
-
小林 智子
化学品検査協会
-
矢吹 増男
萩原工業株式会社 合成樹脂事業部 研究開発センターGL
-
五味 洋子
化学品検査協会
-
伊藤 茂樹
化学品検査協会
-
百武 健一郎
化学品検査協会
-
矢吹 増男
萩原工業株式会社
関連論文
- 1722 生分解性ポリエチレンの研究(その2) : 生分解性複合遮水シートへの適用性
- 高温加熱を受ける繊維補強コンクリートの特性
- 自然界での低密度ポリエチレンの生分解挙動に学ぶ生分解誘引剤の開発と土木分野への応用
- 32年以上土壌埋没したポリエチレンの生分解挙動とその機構
- 自然界におけるLDPE生分解性のフィ-ルドサ-ベイ
- 低密度ポリエチレン(LDPE)の熱酸化劣化と微生物分解に及ぼすジクミルペルオキシド(DCP)の添加効果
- 1469 生物分解性ポリエチレンシートの開発と建築への適用
- 生分解可能澱粉添加プラスチックの土壌埋設による評価研究(第1報)処理条件設定と形態観察を中心とした評価
- 32年以上土壌埋没LDPE,PS,PVC,UFの生分解性の検討
- 生分解可能澱粉添加プラスチックの土壌埋設による評価研究-2-劣化メカニズム解析
- 生分解誘引剤を添加したLDPEの生ゴミ処理による劣化分解促進評価方法の研究
- 32〜37年間生物活性な土壌中に埋没していたLDPEの酸化劣化と分子量変化
- 生分解誘引剤を含有するLDPEの開発と生分解性評価研究
- LDPEの高分子量成分に対する微生物の影響