加圧雰囲気下における高Cr含有鋼の窒素吸放出速度と窒素溶解度
スポンサーリンク
概要
- 論文の詳細を見る
Nitrogen solubility and rate of nitrogen absorption and desorption in High Cr Steel under Pressurized Atmosphere were investigated using pressurized directional solidification furnace. In this study, melting experiments were performed under maximum 1.0 MPa gas condition. It was found that nitrogen solubility was deviated from SievertsLaw over 0.60 mass% nitrogen contents in molten high Cr steel. It was assumed that this phenomenon was not caused by high nitrogen partial pressure but by high nitrogen content in molten high Cr steel. In this study, 1st and 2nd order nitrogen interaction parameters were estimated. And calculated results using estimated parameters were suitable to explain nitrogen solubility of molten high Cr steel. Nitrogen absorption rate was almost same in same nitrogen partial pressure even if total pressure was different. In this study, the apparent mass transfer coefficient in liquid phase of high Cr steel at 1823K was estimated approximately 8.8×10−5 (m·s−1). Nitrogen desorption rate was decreased with increase in total pressure or nitrogen partial pressure. It was indicated that mixed control model of gas phase mass transfer and chemical reaction at gas/liquid interface could be applied to explain nitrogen desorption reaction of molten high Cr steel under pressurized atmosphere.
論文 | ランダム
- 28. 当院における脳卒中リハビリ終了患者の追跡調査(脳卒中)(第17回日本リハビリテーション医学会総会)
- II-A-23.膝関節運動曲線による片麻痺歩行の観察(歩行分析)(第16回日本リハビリテーション医学会総会)
- 184.本態性高血圧症の成因に関する研究 : 交感神経機能,心血行動態,PRA,PVの相関について : 第43回日本循環器学会学術集会 : 高血圧II
- II.1-20.阻害因子としての甲状腺機能低下症(第14回日本リハビリテーション医学会総会)(脳卒中II)
- 3113 高引性耐火モルタルの耐火特性に関する研究(コンクリート系構造部材の耐火性(1),防火)