陰分極法によるDLC膜の欠陥面積の決定
スポンサーリンク
概要
- 論文の詳細を見る
The area of Diamond-like carbon film defects was determined by cathodic polarization. When films cathodically polarized at a potential of -0.8V vs. Ag/AgCl in aerated aqueous Na2SO4 solution, the reduction of oxygen dissolved in the solution took place on the substrate of film defects. The limiting diffusion current of oxygen reduction was proportional to electrode area, so that the area of the film defects could be determined from cathodic current. Although this method is applicable only to insulating films, it has the advantage that it does not damage the substrate. The number, size and distribution of film defects were obtained by Cu electroplating.
- 社団法人 表面技術協会の論文
著者
関連論文
- 鉄-銅系焼結材料の寸法変化率と機械特性
- 混合粉およびメカニカルアロイング粉を用いた銅-ニッケル焼結合金の弾性率と気孔率との関係
- 焼結鋼のヤング率・引張強さと気孔率の関係およびそれら物性値間の相関について
- 焼結鋼の応力-弾性・塑性ひずみ線図の作製および評価
- 静的ヤング率測定値を用いた焼結体の弾性変形解析
- 鉄-銅系焼結材料の硬さとヤング率・ポアソン比との関係
- 応力-ひずみ線図および応力分布に及ぼす焼結体気孔の影響--気孔モデルを用いた有限要素解析
- 鉄-銅系焼結材料の弾性率と気孔率との関係
- 不均一組織を持つ銅-ニッケル焼結合金の弾性率と気孔率との関係
- 焼結鉄の弾性率に及ぼす成形圧力および焼結温度の影響
- ナノインデンテーション法および超音波顕微鏡による顔料入り長油性アルキド樹脂塗膜の劣化評価
- アルミニウム粉末を用いて作製したラネーニッケル陰極の評価
- MgSO_4 と NaHCO_3 混合水溶液による化成処理に及ぼすA3003合金の熱処理の影響
- ベリリウム銅合金の固相溶接に関する研究(第2報) : めっき効果
- ベリリウム銅合金の固相溶接に関する研究(第1報) : 溶接性
- 322 ベリリウム銅合金の固相溶接(第2報) : 棒材の突合せ溶接(Cu・Niめっきの効果)
- 431 ベリリウム鋼合金の固相溶接(第1報) : 板材の重ね溶接
- イオン注入したアルミニウムの耐食性評価
- イオン注入法によるニッケル基合金の耐熱性改善
- VCで被覆した合金工具鋼(SKD 11)および析出硬化系ステンレス鋼(SUS 630)の食塩水中での腐食摩耗について
- TiNで被覆した合金工具鋼(SKD11)の食塩水中での腐食摩耗
- 九州支部主催第4回腐食防食技術研修会 : 実験による腐食防食技術の基礎の修得
- Alイオン注入したNi基合金の高温酸化特性
- 2010年 腐食防食協会九州支部「第167回例会 研究発表会」報告
- 陰分極法によるDLC膜の欠陥面積の決定
- 食塩水中におけるTiN被覆軟鋼と無被覆軟鋼の腐食摩耗について
- TiNで被覆した軟鋼の食塩水中での腐食摩耗について
- 久留米工業高等専門学校