ZrOCl2・8H2OおよびSi(OC2H5)4からのジルコン系粉末の合成
スポンサーリンク
概要
- 論文の詳細を見る
Zircon powders were prepared by means of a sol-gel method from an equimolar mixed solution of Si(OC2H5)4 and ZrOCl2·8H2O dissolved by hot ethanol, and the crystallite growth and phase change in the powders caused by heat treatment were investigated. The formation mechanism and the thermal-decomposition temperature of zircon powders were discussed on the basis of X-ray diffractometry. The results obtained are as follows:(1) The starting temperature of zircon formation in the as-dried powders without grinding treatment was ca. 1500°C and the rate of formation was very slow. On the other hand, the formation of zircon was accelerated by the grinding treatment of the as-dried powders (the starting temperature was ca. 1200°C), and especially the formation reaction was remarkably promoted in the temperature range of 1300-1450°C with the aid of “Hedvall effect” induced by the crystallization of amorphous silica.(2) It was considered that the promotion effect of zircon formation by grinding was attained by the breakdown of siloxane polymers. The formation of zircon took place via the solid-state reaction of tetragonal ZrO2 and SiO2, and silica changed its phase from amorphous (lower temperature) to transition and then to crystal-like (higher temperature) with heat-treatment temperature.(3) It was pointed out that the thermal decomposition temperature of high purity zircon was higher than that reported in literature (1676°C).
- 社団法人 日本材料学会の論文
著者
関連論文
- Si(OC_2H_5)_4 を用いたゾル-ゲル法によるケイ酸塩化合物の合成 : ZrSiO_4 の場合
- 物理化学実験の教材としてのポリアニリン・亜鉛二次電池
- KTP型CsSbO(SiO_3)_2斜方晶の合成
- KTP族化合物,NaSbOSiO_4,KSbOGeO_4,RbSbOGeO_4斜方晶の合成及び焼結
- SiCセラミックの作製 : 薄膜, 焼結体
- SiC, Si_3N_4微粒子の特性に及ぼす粉砕の効果
- 種々の金属窒化物の添加によるSi_3N_4のち密化
- セラミック原料粉末の活性に対する思索
- 炭化ホウ素の焼結に及ぼす助剤の効果
- BeOを添加したα-Si_3n_4粉体の初期焼結性(セラミック材料)
- 炭化ケイ素の焼結に及ぼすメカノケミカル効果
- B_4C/Cサーモカップルを用いた雰囲気炉の温度制御
- ZrO_2-SiO_2系ゲルの調製に及ぼす水の添加量の影響
- ZrOCl2・8H2OおよびSi(OC2H5)4からのジルコン系粉末の合成
- ジルコンの解離温度の検討