BeOを添加したα-Si_3n_4粉体の初期焼結性(<小特集>セラミック材料)

スポンサーリンク

概要

• 論文の詳細を見る

• It is meaningful to understand the relation between the activity of powder evaluated by physicochemical methods and its initial sinterability. In the present work, the influences of powder properties on moldability, initial sintering behavior and microstructual development of sintered body were investigated. The initial sintering of three kinds of silicon nitride powder, LC 10 (code L), H1 (code H) and A-100 (code T), added with 3wt%BeO was performed under nitrogen atmosphere without pressure. The results obtained are as follows : (1) The moldability of the angular shaped powder (T) consisting of aggregated particles was 10w. Between the two fine powders (L, H) consisting of primary particles of irregular shape, the powder (L) having more ultra-fine particles was slightly behind in moldability. (2) If the tendency of densification depend qualitatively on two parameters, i. e., the moldability and the activity for sintering which each powder is possessing, a sequence of the activity per unit particle for sintering was as follows : L>H>T. The sequence agreed with that of specific surface area of powders. However, the densification rate in the initial stage was concluded as follows : H>L>T. (3) The bulk density of sintered body was highest at ca. 1 660℃ for all Si_3N_4. The addition of BeO promoted the α→βi phase transformation and the order of transformation rate accorded with that of initial sinterability. (4) The bulk density of green body increased linearly with an increase of compaction pressure within the range of 3 ton/cm_2, and the compaction pressure had no connection with the α→β transformation.

• 社団法人日本材料学会の論文
• 1987-01-15

著者

• 菅野 善則

  名古屋工業技術試験所

関連論文

• BeOを添加したα-Si_3n_4粉体の初期焼結性(セラミック材料)
• 炭化ケイ素の焼結に及ぼすメカノケミカル効果
• B_4C/Cサーモカップルを用いた雰囲気炉の温度制御
• ZrOCl2・8H2OおよびSi(OC2H5)4からのジルコン系粉末の合成
• ジルコンの解離温度の検討

スポンサーリンク