• In the first report, we have proposed “matrix brick” which is made of quartz flour through the 1600 hole/cm2 sieve mixed with abt. 5% of CaO. In mixing this “matrix” with varions amounts of coarer grains (400-1600 hole/cm2), we found that the sample cones containing less than 30% of “matrix” are more refractory, and therefore such bricks are good for use in open-hearth roof.In the second report, results of dilatometric experiments and microscopic observations of matrix bricks are given. There are two remarkable periods of mineral development during the sintering of matrix bricks; i.e.1000-1200°C cristobalite development1200-1400°C tridymite developmentThe formation of tridymite was detected byT1-inversson (α→β1 trid.) in samples fired at lower temperaturesT2-inversion (crist.→trid.) in samples fired at higher temperaturesBy comparing parmanent expansions at 1000°C in reheating the bricks, a minimum was found in samples fired at 900-1100°C, Milk of lime in green body gradully absorbs CO2 and is converted into CaCO3 at abt. 600°C, then it decomposes. At abt. 800-900°C, formation of calcium silicate was concluded from a marked shrinkage, and at abt. 1400°C it became visible under a microscope in forming ring-like shaped crystals. When fired at above 1400°C, calcium silicate diffused into the matrix, but when cooled, it recrystallized again.In the present (third) report, experimental results of parmanent expansion, porosity, apparent density and permeability are given.In the firing range of 1100°-1200°C, the apparent specific gravity of the matrix bricks has decreased from 2.60 to less than 2.40, but the porosity has also decreased and the crushing strength increased. Because there is no great change of porosity during firing, it is advisable to make quality control in green body. Increase of CaO content is good for crystal growth of Tridymite but rather decreases the its amount, and makes expansion smaller.

• 社団法人 日本セラミックス協会の論文

著者

• 滑石 直幸

  播磨耐火煉瓦

• 須賀 音吉

  播磨耐火煉瓦

関連論文

• 59 広畑転炉工場における炉体煉瓦原単位の低減策について(転炉, 日本鉄鋼協会第 69 回(春季)講演大会講演論文集 (I))
• 64 耐食性軟質スリーブ煉瓦の実用試験について(製銑および製鋼, 第 55 回講演大会講演大要)
• 61 塩基性製鋼転炉用マグネシアーカルシア系耐火物の溶融損傷反応に関する鉱物学的研究(転炉, 製鋼, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
• 10.耐火煉瓦に及ぼすNa_2O-V_2O_5の影響(研究発表講演要旨)
• 84 純酸素上吹転炉内張使用後煉瓦の研究(製鋼・転炉, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
• 熔鉱炉煉瓦製造を目的とする米国産粘土の性状
• 礬土 : 珪酸系耐火物のマトリツクスの研究
• 各種原料の燒成過程における物理牲の變化 : 珪石煉瓦のMatrixの研究 (第3報)
• 珪石煉瓦のMatrixの研究 (第2報) : 煉瓦焼成過程におけるMatrix部の生成進化の観察
• 珪石煉瓦のMatrixの研究 (第1報) : Matrixの決定と二三の問題

スポンサーリンク