石油樹脂のジアゾニウム塩の反応
スポンサーリンク
概要
- 論文の詳細を見る
Petroleum resin was nitrated, reduced, and diazotized. Decomposition of the resultant diazonium chloride in aqueous methanol was found to follow the firstoorder kinetics and showed rate constants of 3.43, 5.84, and 45.40 x 10<SUP>-5</SUP> sec<SUP>-1</SUP> at 11°C, 20°C, and °C, respectively, the apparent activation energy being 9030 cal/mol.<BR>Upon decomposition, the petroleum resin molecule formed radicals, which served as sites for grafting with acrylamide. Thegraft reactions were carried out in acidic and alkaline media at 90°C and 95°C. The products were fractionated and examined by means of infrared spectrophotometry.<BR>The effects of ferric chloride catalyst and the amount of the monomer were investigated. It was suggested that only a part of the macroradicals so formed were able to initiate the graft reactions.
- 社団法人 有機合成化学協会の論文
著者
関連論文
- デンプンの化学 : その工業化学的利用を中心として(天然高分子の化学)(高分子化学)
- アタクチックポリプロピレンの塩素化 : ポリオレフィンの高分子反応に関する研究 (第1報)
- 水溶性高分子化合物に関する研究-11-:ポリ-2-メチル-N-ビニルイミダゾールの電離性
- 水溶性高分子化合物に関する研究-10-アクリルアミドとマレイン酸およびフマル酸の共重合
- 石油樹脂のジアゾニウム塩の反応
- ジカルボン酸ジグルコースエステルの合成
- 高分子アゾ染料について-1-
- クロトン酸およびイソクロトン酸の共重合性
- 水溶性高分子の機能 (水性高分子の応用)
- エチレンイミン誘導体に関する研究-3-
- 水溶性高分子についての二三の問題
- ブチルアルデヒド中でのアクリルアミドのテロメル化について(水溶性高分子化合物に関する研究-4-)
- ポリ(2-メチル-N-ビニルイミダゾール)とn-アルキルブロミドとの反応
- ボリアクリルアミドのN-メチロール化とN-ジメチルアミノメチル化について(水液性高分子化合物に関する研究-3-)
- Studies on the Water-Soluble Polymers. II.:Polymeric Hydrazine Compounds. (1)
- Studies on Ethyleneimine Derivatives. II:Applications to finishing of Textile Fabrics