2-Methyl-N-vinyl imidazole was polymerized in methanol to give a water-soluble polymer with intrinsic viscosity of 3.20 as determined in 0.1 N hydrochloric acid at 30°C. The titration curves measured in the presence and the absence of potassium chloride indicated that the monomer behaved as an ordinary base of strength pK<SUB>a</SUB>=7.75. The polymer gave a highly extended titration curve characteristic of polyelectrolyte. In a wide range of the ionization degree β, the following equation derived by the theory of Katchalsky, et al. was obeyed. pH=pK<SUB>o</SUB>-log[β/(1-β)]-2.19β where pK<SUB>o</SUB> is 6.5. When compared with polyethyleneimine, the poly(1-methyl-N-vinyl imidazole) having weaker basicity seemed to have rather rod-like shape in aqueous solution. Its broad application to industry as a useful cationic polyelectrolyte is expected.
- 社団法人 有機合成化学協会の論文
著者
関連論文
- デンプンの化学 : その工業化学的利用を中心として(天然高分子の化学)(高分子化学)
- アタクチックポリプロピレンの塩素化 : ポリオレフィンの高分子反応に関する研究 (第1報)
- 水溶性高分子化合物に関する研究-11-:ポリ-2-メチル-N-ビニルイミダゾールの電離性
- 水溶性高分子化合物に関する研究-10-アクリルアミドとマレイン酸およびフマル酸の共重合
- 石油樹脂のジアゾニウム塩の反応
- ジカルボン酸ジグルコースエステルの合成
- 高分子アゾ染料について-1-
- クロトン酸およびイソクロトン酸の共重合性
- 水溶性高分子の機能 (水性高分子の応用)
- エチレンイミン誘導体に関する研究-3-
- 水溶性高分子についての二三の問題
- ブチルアルデヒド中でのアクリルアミドのテロメル化について(水溶性高分子化合物に関する研究-4-)
- ポリ(2-メチル-N-ビニルイミダゾール)とn-アルキルブロミドとの反応
- ボリアクリルアミドのN-メチロール化とN-ジメチルアミノメチル化について(水液性高分子化合物に関する研究-3-)
- Studies on the Water-Soluble Polymers. II.:Polymeric Hydrazine Compounds. (1)
- Studies on Ethyleneimine Derivatives. II:Applications to finishing of Textile Fabrics