The dynamic compressive fracture of vacuum-evaporated gold films in the thickness range 450 to 3300Å was observed directly in a scanning electron microscope and a transmission electron microscope by mounting the film on uniblock substrates. Electron microscopy observations of heat-treated films showed a wavy type fracture by the dynamic compressive-type strain. This fracture propagation was clearly observed in regions of circular convex domes (3-50 μm diam.) and holes. The distribution of slip within the fracture tip plastic zone was markedly dispersed. The fracture strain increased with increasing film thickness, the greatest increase occurring above 3000Å. The fracture strain ratio (ε<SUB>d</SUB>ε<SUB>s</SUB>) of dynamic and static fracture gold films thicker than about 2000Å was usually of the order of 1.1 to 2.4.
- 日本真空協会の論文
著者
関連論文
- St. Helens 火山の火口温度(1980 年 7 月 28 日測定)
- コースティックス法によるA7075-T6の衝撃破壊に関する研究
- C, Al, W, Cr 混入 Au 膜の機械的性質
- C, W, Al混入Au膜の引張り破壊
- Mo,W混入多層Au膜の引張り破壊
- 3層Au蒸着膜の引張り破壊に及ぼす不純物の効果 (第31回真空に関する連合講演会プロシ-ディングス)
- 2層Au膜の引張り破壊に及ぼす不純物の効果 (第30回真空に関する連合講演会プロシ-ディングス)
- Au蒸着膜の引張り破壊に及ぼす不純物の効果
- Au蒸着膜の擬圧縮変形サイクル下における疲労類似破壊挙動
- Au蒸着膜の疲労破壊
- Au蒸着膜の擬圧縮破壊-2-
- Au蒸着膜の擬圧縮破壊-1-
- Au蒸着膜の引張り破壊-4-
- Au蒸着膜の引張り破壊-3-
- Au蒸着膜の引張り破壊-2-
- Au蒸着膜の引張り破壊
- 三層Au蒸着膜の引張り破壊に及ぼす不純物の効果
- 二層Au膜の引張り破壊に及ぼす不純物の効果
- Au蒸着膜の引張り破壊に及ぼす不純物の効果
- Au蒸着膜の擬圧縮変形サイクル下における疲労類似破壊挙動
- Au蒸着膜の擬圧縮破壊 (II)
- Au蒸着膜の擬圧縮破壊 (I)
- Au蒸着膜の疲労破壊
- Au蒸着膜の引張り破壊 (II)
- Au蒸着膜の引張り破壊 (IV)
- Au蒸着膜の引張り破壊 (III)
- Au蒸着膜の引張り破壊
- Au薄膜の付着破壊に及ぼすアモルファスSbの効果