コバルト添加酸化鉄の磁気的性質(第2報) : エピタキシャル型酸化鉄の生成と磁気特性

概要

論文の詳細を見る
Acicular γ-Fe2O3 particles were treated at 90°C in alkali solution containing CO2+ and Fe2+. The coercivity of resultant particles remarkably increased with increasing CO2+/Fe2+ ratio, and reached a maximum value in the vicinity of 0.4 to 0.5. The increase of coercivity was attributed to the magnetic anisotropy of iron-cobalt ferrite which was considered to crystallize at the surface of γ-Fe2O3. The magnetic properties of γ-Fe2O3 particles coated by iron-cobalt ferrite, such as a variation of coercivity in annealing at 60°C or printing effect, were extremely stable compared with those of cobalt-substituted iron oxides.
社団法人粉体粉末冶金協会の論文