Bi系酸化物超電導体の超電導特性に及ぼす中間縮の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effect of a combination process with intermediate pressing and sintering on critical current density, Jc, has been studied for the high-Tc Bi system with the nominal composition of Bi<SUB>1.6</SUB> Pb<SUB>0.5</SUB> Sr<SUB>2.0</SUB> Ca<SUB>2.0</SUB> Cu<SUB>3.0</SUB> O<SUB>z</SUB> . The Jc of the plate samples has increased drastically from 200 to 2000 A/cm2 by repeating this process more than one time . A micro-hardness Hv, has been measured as a function of the depth from the sample surface . The Hv in the sample has the maximum value of about 80 on the surface and decreases to 50 at depth below 2mm . From the estimation of experimental data, it has been found that the Jc increases exponentially with the Hv.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 531 CBNビトリファイドホイールの研削性能に及ぼす組織均一化の影響(OS11 研削・砥粒加工)
- 異種混合砥粒を用いた高性能ビトリファイド砥石の開発研究
- 組織の均一化に基づく高性能ビトリファイドcBNホイールの開発研究
- プラズマ溶射法で作製したBi2223酸化物円筒の超伝導磁気シールド特性
- 脳磁気計測用超伝導磁気シールド容器の開発
- セリア系電解質を用いた中温作動型燃料電池 (資源・素材技術の最近の進歩--平成19年度全国鉱山・精錬所現場担当者会議講演集 資源 精錬 新素材)
- 技術情報 セリア系電解質を用いた低温動作可能なSOFC
- 無電解めっき処理による亜鉛合金金型の表面損傷の防止
- 無電解めっき処理金型の機能特性に関する研究-2-実機金型への適用
- 無電解めっき処理金型の機能特性に関する研究-1-亜鉛合金への適用
- フレッチング損傷防止に関する研究-各種窒化処理について-
- 無電解ニッケルめっきによるフレッチング・コロ-ジョンの発生防止に関する研究-2-高強度材への適用および寸法効果の検討
- 無電解ニッケルめっきによるフレッチング・コロ-ジョンの発生防止に関する研究
- Bi系酸化物超電導体の超電導特性に及ぼす中間縮の影響
- Bi系酸化物超電導体の超電導特性に及ぼす冷却速度の影響