Ti-M-TiC (M: Cr, Mo, W)硬質焼結材料の組織と機械的性質
スポンサーリンク
概要
- 論文の詳細を見る
Ti-8.4vol%M-47.4vol%TiC (M: Cr, Mo, W) alloys were prepared through P/M technology and their microstructures and mechanical properties were investigated. It was revealed that Ti-Cr-TiC alloy (Cr alloy) had 3 phases, which were TiC, α-Ti and β-Ti, Ti-Mo-TiC alloy (Mo alloy) had 2 phases, which were TiC and β-Ti and Ti-W-TiC alloy (W alloy) had 3 phases, which were TiC, β-Ti(Ti rich) and W(β-Ti type, W rich). It was noted that TiC grain size of W alloy was much smaller than that of both Cr alloy and Mo alloy. It was found that hardness and transverse-rupture strength of W alloy were much higer than those of both Cr alloy and Mo alloy.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- チタン基焼結硬質合金の開発と腐食特性に関する研究
- WC-(0-16)mass%Cr_3C_2-15mass%Ni超硬合金の組織と機械的特性及び腐食特性
- Cu-W/Cu複合材料の諸性質に及ぼす溶浸条件の影響
- 超硬合金摺動面の微細き裂発生機構
- Ti-Mo-Tic硬質焼結材料の組織と機械的性質に及ぼすMo添加量の影響
- Ti-Mo-TiC焼結合金におけるTiCの腐食挙動
- メカニカルシール超硬合金しゅう動リングのき裂発生機構 : 第3報, 熱弾塑性解析による諸因子の評価
- 金属粉末射出成形法によるTi基硬質焼結材料の開発
- 金属粉末射出成形法による焼結Co-Cr-W-C合金の創製
- Ti-Mo系焼結合金のNaOH溶液中の腐食挙動
- β-Ti基硬質焼結材料の開発
- Ti-Mo系焼結合金の腐食挙動について
- Ti-M-TiC(M:Cr,Mo,W)硬質焼結材料の組織と機械的性質 (硬質材料)
- チタン基硬質焼結材料の開発 (硬質材料)
- 超微粒WC-Co超硬合金の組織と抗折力
- WC-Cr3C2-15%Co超硬合金の組織と機械的性質
- 超硬合金に対する添加炭化物としてのTaCとNbCの役割の差
- HIP 処理を行った液相焼結 SiC セラミックスの諸特性
- チタン-モリブデン合金溶射皮膜の耐食性
- 超硬合金と鉄鋼材料との電位差腐食の研究
- 超硬合金の水溶液中腐食に及ぼすNaCl濃度の影響
- 焼結硬質合金の腐食挙動に関する研究
- WC - Co系超硬合金の腐食特性に及ぼすWC粒子径の影響
- WC-Ni-Cr_3C_2系超硬合金の定電位分極による腐食反応調査
- PIMプロセスによるAl_2O_3-30mass%TiC複合材料の開発
- 記念講演論文 粉末冶金法によるチタン基焼結合金の開発と諸特性
- WC-Ni-Cr系超硬合金のNaOH溶液中での腐食挙動
- Ti-Mo系焼結合金に形成される不働態被膜の構造
- WC-Ni-Cr系合金の腐食特性に及ぼすCr, Cの影響
- アクリルーアタクチックポリプロピレンーワックス系バインダーのMo粉末の射出成形への応用
- Ti-M-TiC (M: Cr, Mo, W)硬質焼結材料の組織と機械的性質
- チタン基硬質焼結材料の開発
- 超微粒WC-Co超硬合金の組織と抗折力
- WC-Cr3C2-15%Co超硬合金の組織と機械的性質
- 超硬合金に対する添加炭化物としてのTaCとNbCの役割の差
- 高クロム鋳鉄溶浸超硬合金の諸性質
- WC-Ni系超硬合金のH2-CH4雰囲気予備焼結
- ポアを分散させた摺動用超硬合金の製造とその諸性質
- WC-(Fe-Cr-C)系焼結超硬合金の諸性質