有機化合物の加圧焼結過程における空孔構造変化
スポンサーリンク
概要
- 論文の詳細を見る
Changes in the pore structure were searched by the measurement pore size distribution and cumulative pore volume, on cinnamic acid and adipic acid compacts hot-pressed at various temperatures and pressures. Studies are mainly on the initial and intermediate stages of the densification during which plastic flow mechanism predominates. When hot-pressed under the constant pressure, the total pore volume decreased rapidly with increasing temperature, particularly near the melting point, and pores shrank uniformly with keeping their similar shape. On the other hand, when hot-pressed under the constant temperature, pore volume decreased with increasing pressure but the degree of volume decrease became less when the pressure was high. Furthermore the larger pores shrank rapidly than the smaller ones in contrast to the former case.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 排出管を付設したホッパよりの粉体の流出に及ほす粒径の影響
- 顆粒強度の直接および間接測定
- 混合粉体の摩擦および付着に及ぼす粒径比の効果
- 加圧圧縮過程の初期段階におけるヘマタイト顆粒強度の影響
- 顆粒の圧縮成形過程における顆粒間および顆粒内空隙の変化
- PZTセラミックスの製造における混合方法の影響
- 粉体層の底圧による粉体の内部摩擦の測定
- ポリスチレン粉体の成形物の構造に及ぼす成形圧力および温度の影響
- BaCO3とGeO2の反応
- BaCO3とTiO2の反応の速度論的研究
- プラスチック粉体成形物の空孔構造
- 粉体の流動性測定の試み
- 低融点化合物による加圧焼結機構の研究 : 安息香酸結晶粉末の加圧焼結
- BaCO3-TiO2二元系固体反応の速度と機構に及ぼす反応物粒子の凝集の影響
- MnLiZnフェライト顆粒の強度と圧縮挙動
- NiO-MoO3 2成分系固相反応速度に対する単独および混合摩砕の効果
- 粉体の濡れ
- 円の二次元充てん模型による数値計算
- 粉体の濡れ
- 低融点化合物による加圧焼結機構の研究-2-
- 有機化合物の加圧焼結過程における空孔構造変化
- 混合粉体の摩擦および付着に及ぼす粒径比の影響