Al2O3/TiC複合材料のミクロ・ナノ構造と特性 (ナノメ-タコンポジット材料)

スポンサーリンク

概要

• 論文の詳細を見る

• High density Al<SUB>2</SUB>O<SUB>3</SUB>/TiC composites were fabricated by a conventional hot-pressing of mixtures of Al<SUB>2</SUB>O<SUB>3</SUB> and TiC powders at 1700-1900°C in Ar atmosphere. Transmission electron microscopic observations revealed that TiC particles were dispersed not only at grain boundaries but also within Al<SUB>2</SUB>O<SUB>3</SUB> matrix grains. The mechanical properties of these composites were considerably improved by dispersed TiC particles. The fracture toughness of these composites increased from 4MPam<SUP>1/2</SUP> to 6MPam<SUP>1/2</SUP> and the fracture strength also increased from 550MPa to 1100MPa. The effect of TiC dispersions in Al<SUB>2</SUB>O<SUB>3</SUB> grains on the mechanicai properties such as strength, toughness and hardness were discussed.

• 社団法人 粉体粉末冶金協会の論文

著者

• 新原 晧一

  大阪大学 産業科学研究所

• 中平 敦

  大阪大学 産業科学研究所

• 竹之内 武義

  三菱マテリアル(株)セメント研究所

• 松木 竜一

  三菱マテリアル(株)セメント研究所

• 上田 尚郎

  三菱マテリアル(株)セメント研究所

関連論文

• マシナブルSiCのノナ構造
• 高圧鋳造法によるチタン酸カリウム・ウィスカ強化アルミニウム合金の製造
• 新しい双方向ナノ構造を持つ耐衝撃性に優れたセリア系ジルコニアナノ複合セラミックスの開発
• 2層構成のAl2O3複合材の焼結と機械的特性
• Si3N4-SiCナノ複合体の耐酸化性
• 高温超強度Si3N4-SiCナノ複合材料
• 天然ムライト複合体の作製と評価 (ミクロ複合材料・ナノ複合材料)
• 天然ムライト/SiCナノ複合材料の機械的性質の改善 (ナノメ-タコンポジット材料)
• Al2O3/Wナノ複合材料の作製 (ナノメ-タコンポジット材料)
• Al2O3/TiC/ZrO2複合材料の微細組織と機械的性質 (高次制御材料-1-)
• Al2O3/TiCナノ複合材料の常圧焼結 (高次制御材料-1-)
• タイトル無し
• Al2O3/TiC複合材料のミクロ・ナノ構造と特性 (ナノメ-タコンポジット材料)
• タイトル無し

もっと見る 閉じる

スポンサーリンク