チタン酸バリウム微粒子の構造と誘電性

スポンサーリンク

概要

• 論文の詳細を見る

• Fine particles of high-purity barium titanate from a minimum of 500A upwards were prepared. by the thermal decomposition of barium titanyl oxalates, BaTiO(C<SUB>2</SUB>O<SUB>4</SUB>)<SUB> 2</SUB>⋅4H<SUB>2</SUB>0, at 600-1100°C. The effective dielectric constant was measured with the particles dispersed in Araldite resin. The following results are of interest: (1) In the case of fine particles of 500-700A, the effective dielectric constant delineates a smooth curve with temperature and the ferroelectric Curie peak moves to low temperature. (2) From X-ray diffraction analysis, the tetragonality decreased with decreasing particle size, thus leading to cubic symmetry.<BR>A brief discussion was given to the correlation between the decrease in tetragonality and the shift of the Curie point.

• 社団法人 粉体粉末冶金協会の論文

著者

• 西本 幸三

  日本電気株式会社 中央研究所

• 五嶋 康雅

  京都大学理学部

• 中西 典彦

  京都大学理学部

• 可知 〓次

  京都大学理学部

• 西本 幸三

  日本電気株式会社

関連論文

• フェライト薄膜磁気ディスクのノイズ特性
• チタン酸バリウムの相転移におよぼす一軸加圧効果
• チタン酸バリウム微粒子の構造と誘電性
• 溶浸法の発達について
• オートラジオグラフィーによる銀の焼結機構の研究
• BaTiO_3-BaB_2O_4系状態図とその熔融物からのBaTiO_3結晶の育成
• BaO-Fe2O3凝相系平衡状態図について
• ニッケル微粒子の構造と触媒活性

スポンサーリンク