耐酸化性タングステン焼結体について-2-
スポンサーリンク
概要
- 論文の詳細を見る
Tungsten-chromium sintered compacts were hot-pressed at 1450°C for 30 min in graphite moulds. Mechanical properties and high-temperature oxidation resistance of sintered compacts were tested. And also the improvement of oxidation resistance by small additions of Al and Si was tested.<BR>Results obtained are summarized as follows.<BR>(1) The density of the hot-pressed specimens were more than 95% of the theoretical value.<BR>(2) The hardness of the sintered compacts was HRC 56.6-63.0, higher than the hardness of tungsten.<BR>(3) Transverse rupture strengths of 30-40kg/mm<SUP>2</SUP> were obtained.<BR>(4) The addition of Cr (>30 wt%) was found to improve the oxidation resistance.<BR>(5) (W-30 Cr)-Si alloy was suitable for tungsten-base high temperature materials.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 窒化処理したチタンカーバイド系サーメット工具
- 球状黒鉛鋳鉄による鋼管の鋳ぐるみ接合について
- 炭化タングステンのペ-スト被覆
- Ti-Mo系焼結体の研究(第1報)
- Ti-Mo系焼結体の研究 (第2報) Ti-Mo系焼結体の諸性質の改善
- 線爆発による粉末の生成とその特性(第1報)
- 水銀ランプ用焼結型電極の研究
- 線爆発による粉末の生成とその特性(第2報)
- 耐酸化性タングステン焼結体について-2-
- 低温焼結タングステン体について-4-W-Ni-P合金の機械的性質
- 低温焼結タングステン体について-3-Pd添加の影響
- 低温焼結タングステン体について-1-W-NiP合金の焼結特性
- 耐酸化性タングステン焼結体について-1-