噴霧Fe-Cu合金粉の2,3の性質
スポンサーリンク
概要
- 論文の詳細を見る
An attempt to eliminate complicated phenomena of Fe-Cu compacts during sintering, Fe-Cu prealloyed powders were produced by liquid atomization, and their pressing and sintering properties were examined. The results were summerized as follows:<BR>(1) The suitable annealing condition to obtain good compressibility of atomized powders is of 900°C for 1 hour in hydrogen.<BR>(2) Weight loss in Rattle test and transverse rupture strength of compacts pressed at 5t/cm<SUP>2</SUP> are in the range of 0.5-2.0% and 0.7-1.2 Kg/mm<SUP>2</SUP>., respectively.<BR>(3) With increasing Cu content, sintering properties of Fe-Cu alloyed powders are improved.<BR>(4) Compacts pressed at 5t/cm<SUP>2</SUP> and sintered at 1200°C for 1 hour in hydrogen show the tensile strength of 27.6 Kg/mm<SUP>2</SUP> for 5%Cu and 44.0 Kg/mm<SUP>2</SUP> for 20%Cu., respectively.
- 社団法人 粉体粉末冶金協会の論文
著者
-
武田 徹
科学技術庁金属材料技術研究所
-
田村 皖司
科学技術庁金属材料技術研究所
-
宮本 憲治
住友金属特殊株式会社
-
武田 徹
科学技術庁 金属材料技術研究所
-
田村 皖司
科学技術庁 金属材料技術研究所
関連論文
- 9. 加工学・加工機器 9.4 粉体加工 (機械工学年鑑 "JSME Year Book")
- 9. 加工学・加工機器 9・4 粉体加工 (機械工学年鑑 "JSME Year Book")
- 水噴霧Ni-20%Cr super finesの焼結性
- W-Cr合金の耐酸化性に及ぼすPd添加の影響
- 高密度W-Cr焼結合金の製造とその酸化特性
- ステンレス鋼圧粉体の焼結に伴う緻密化について
- Cr-Niオーステナイト・ステンレス鋼粉の圧縮成形ならびに焼結
- センダスト合金の粉末圧延法とそれらの電磁気的特性
- 粉末圧延法によるチタン薄板の製造
- 噴霧Fe-Cu合金粉の2,3の性質
- スリップキャスチング法による協会賞賞牌の製造について(資料)
- Liquid atomizationによる13Crステンレス鋼粉の製造
- 粉末圧延法によるステンレス鋼薄板の製造
- 粉末圧延法によるFe-Cuクラッド板の製造