QMG法により作製されたYBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-x</SUB>の結晶学的キャラクタリゼーション
スポンサーリンク
概要
- 論文の詳細を見る
The bulk material of YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-x</SUB> prepared by the Quench and Melt Growth (QMG) process was characterized from crystallographic points of view. It was shown that the QMG-processed material was a composite of YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-x</SUB> (123) matrix and Y<SUB>2</SUB>BaCuOy (211) dispersoids. Because the material was highly oriented, analysis of the crystal structure was carried out by means of a modified method of texture analysis. It was found that the matrix consisted of only a few twinned crystallites of the order of 10<SUP>-2</SUP>m which were related to each other with boundaries of little difference in angle. The material was concluded to be a large grain composed of 123 crystallites containing a fine dispersion of 211 phase.
著者
-
木村 正雄
新日本製鐵株式会社先端技術研究所
-
澤野 清志
新日鐵(株) プロセス技術研究所
-
木村 正雄
新日鐵(株)第一技術研究所
-
林 昭彦
新日鐵(株)第一技術研究所
-
森田 充
新日鐵(株)第一技術研究所
-
松尾 宗次
新日鐵(株)第一技術研究所
-
澤野 清志
新日鐵(株)第一技術研究所
関連論文
- 3p-ZA-7 QMG法により作製したYBa_2Cu_3O_のキャラクタリゼーション I
- 5p-PS-105 Pr置換によるYBaCuOの超伝導の消失
- 5p-PS-103 BiSrCaCuの超伝導特性
- カーボンレス高アルミナ質浸漬ノズルの開発
- 鉄鋼表面の大気反応生成物のミクロ形成過程と局所構造
- 耐候性鋼に形成されるさびのFe(O, OH)_6ネットワーク構造
- 放射光イメージングプレートシステムを用いた高温反応の in situ 観察技術(微小域構造解析)(最先端の化学分析と物理解析)
- 5p-PS-104 YBaCuOの超伝導特性に及ぼすFe添加の影響
- 放射光による鉄鋼材料の表面/界面の研究
- さびでさびから鋼を守る : さび形成反応のメカニズム解明とその制御
- 放射光を用いた表面・界面での反応のその場(in situ)観察
- 放射光を用いた表面・界面の反応観察
- 溶射によるZG質耐火物の高耐用化
- 大粗粒添加不定形耐火物の機械的性質(その2)
- CCパウダーの改善による浸漬ノズル寿命向上
- 耐候性鋼のメスバウアー分光による解析
- Ni添加耐候性鋼の腐食生成物のTEM観察
- 3%Ni添加海浜型耐候性鋼の腐食生成物の観察
- 技術論文 耐候性鋼に形成されるさびのFe(O,OH)6ネットワーク構造と耐食性 (防食技術特集)
- 耐候性鋼に形成される錆び層のミクロ構造
- 放射光による鉄鋼表面/界面の研究 : 腐食の in situ 観察
- 耐候性鋼に形成される腐食生成物の微細構造
- 積層構造を持つ系のモデルハミルトニアン
- 大粗粒添加不定形耐火物の機械的性質(その1)
- 鉄が濡れるとどうなるか? : 液体/金属界面の反応観察
- QMG法により作製されたYBa2Cu3O7-xの結晶学的キャラクタリゼーション
- 大気腐食のメカニズム解明のための材料構造科学的アプローチ