ゾルーゲル法によるBi2Sr2Ca2Cu3Ox超伝導セラミックスの作製

概要

論文の詳細を見る
High Tc phase with c=3.7 nm of Bi2Sr2Ca2Cu3Ox was synthesized from powder prepared by Sol-Gel method. The sol was prepared from strontium acetate, calcium acetate, copper acetate and bismuth ethoxide. When powdering-sintering cycles were repeated four times with total sintering time of 148 h at 845°C-850°C, the amount of the high Tc phase in the specimen with starting composition ratio of 2:2:2.2:3.2, was larger than 95% from XRD measuerment. Tcoffset of the specimen was of 90K. From the sol descrived above, gel fibers with a length of 1 m and a diameter of 100 μm to 300 μm were successfully drown. After sintering at 845°C for 5 h, ceramic fiber of which Tconset, was of 110K were obtained.
社団法人粉体粉末冶金協会の論文