電子線照射による金属クラスターの“構造ゆらぎ”
スポンサーリンク
概要
- 論文の詳細を見る
The gold clusters, less than 50 A in diameter, became structurally unstable under the electron beam irradiation (10<SUP>5</SUP> electrons/A<SUP>2</SUP>. sec) and continually changed their shapes; single, twinned and multiply-twinned crystals. Two possibilities for causing the instability can be thought; specimen temperature rise or surface charging due to secondary electron emission. Electron microscope observation utilizing a fine-focused electron beam favors to the surface charging effect. Reorganization of atoms in the clusters, often undergoing in the twin deformation, was caused by a shear stress due to a coulomb force arising from the positive surface charges.
- 日本結晶学会の論文
著者
関連論文
- 12p-N-3 微粒子線の実験I. : 粒子速度の測定
- 4a-S-3 Au超微粒子の微細構造
- 12p-N-4 微粒子線の実験II : 粒子の成長機構
- 電子線照射による金属クラスターの“構造ゆらぎ”
- 4p-M-7 γ-Al_2O_3の結晶構造解析(I)
- 4p-E-3 TEMによる結晶表面原子の直接観察
- 3a-P-2 酸化物超微粒子の生成
- 12a-W-5 結晶欠陥の電顕観察
- 27p-F-5 非晶質の電顕観察の動向
- 27a-LC-3 超微粒子の構造(新物質相(超微粒子,人工格子,アモルファス,準結晶,液体)の構造と物性-何がどこまでわかったか-,格子欠陥,金属,磁性,X線粒子線合同シンポジウム)
- タイトル無し
- 31a-A3-10 微粒子線の実験IV(31a A3 X線・粒子線,X線・粒子線)
- 30a-BG-12 金属クラスターの安定性の研究(30a BG 表面・界面)
- 30a-BG-11 金属クラスター(粒径10A)の電顕観察(30a BG 表面・界面)
- 1p-A6-3 金属超微粒子(
- 31p-A3-2 γ-Al_2O_3の結晶構造解析(II)(31p A3 X線・粒子線,X線・粒子線)