Determination of Activities in Slags Containing Chromium Oxides.
スポンサーリンク
概要
- 論文の詳細を見る
Activities of CrO and CrO1.5 were determined in slags based on the systems of CaO-SiO2-CrOx, CaO-SiO2-MgO-CrOx, CaO-SiO2-Al2O3-CrOx, and CaO-SiO2-MgO-Al2O3-CrOx with electro-motive force method. Equilibrium was achieved between Cr-saturated CrAg alloy and slags. Effects of temperature and slag composition on the activities of chromium oxides and the oxidation state of chromium in the slags were investigated. Chromium oxides activities decreased but the divalent chromium fraction in the slags increased when elevating temperature in the range of 1500-1600°C. The slag basicity has a significant effect, the higher the slag basicity, the higher the activities of chromium oxides, and the lower the divalent chromium fraction. By partial substituting MgO for CaO, activities of CrO and CrO1.5 will decrease, but the effect on the oxidation state of chromium in the slag is not obvious. Increasing Al2O3 content from 0 to 10 mol% results in higher activities of chromium oxides and lower divalent chromium fraction. Further increasing of Al2O3 content to 20 mol% does not cause any significant effect. In addition, activities of chromium oxides and oxidation state of chromium in a FeCr type slag system were examined.
著者
-
Holappa Lauri
Laboratory Of Metallurgy Helsinki University Of Technology
-
Xiao Yanping
Laboratory of Metallurgy, Helsinki University of Technology
関連論文
- Unusual Wetting of Liquid Bismuth on a Surface-Porous Copper Substrate Fabricated by Oxidation-Reduction Process
- Wettability of Liquid In and Bi on Flat and Porous Solid Iron Substrate
- Estimation of Surface Tension of Molten Silicates Using Neural Network Computation
- Evaluation of the Surface Tension of Ternary Silicate Melts Containing Al_2O_3, CaO, FeO, MgO or MnO
- Fluid Flow and Free Surface Phenomena in Rotary Electromagnetic Stirring of a Metallic Melt
- A Model for Estimating Viscosities of Aluminosilicate Melts Containing Alkali Oxides
- Surface Tension Evaluation of Molten Silicates Containing Surface-active Components (B_2O_3, CaF_3 or Na_2O)
- Characteristics of Iron Entrainment into Slag Due to Rising Gas Bubbles
- Mechanisms of Iron Entrainment into Slag due to Rising Gas Bubbles
- Coupled Simulation of Heat Transfer and Phase Transformation in Continuous Casting of Steel
- Determination of Activities in Slags Containing Chromium Oxides.