Characteristics of Iron Entrainment into Slag Due to Rising Gas Bubbles
スポンサーリンク
概要
- 論文の詳細を見る
Iron droplets can be entrained into the slag phase when gas bubbles pass through the molten iron/slag interface. The entrainment phenomena occurring during passage of single bubbles through the interface were investigated by using in-situ X-ray transmission (fluoroscopic) techniques and by collecting and measuring the entrained iron droplets. The effects of bubble size, interfacial tension and viscosity of the slag on the iron droplets entrainment were investigated. The results showed that the mass of the entrainment increased with the increasing bubble size, but decreased with increasing interfacial tension and slag viscosity. A dimensionless equation was proposed to describe the relation between the entrainment of metal into slag and the above-mentioned parameters. This information can be used to optimize heat and mass transfer processes e.g. in ladle metallurgy and to reduce the financial loss due to metal discard within the slag.
- 社団法人 日本鉄鋼協会の論文
- 2003-11-15
著者
-
Holappa Lauri
Laboratory Of Metallurgy Helsinki University Of Technology
-
Han Zhijun
Laboratory Of Metallurgy Helsinki University Of Technology
関連論文
- Unusual Wetting of Liquid Bismuth on a Surface-Porous Copper Substrate Fabricated by Oxidation-Reduction Process
- Wettability of Liquid In and Bi on Flat and Porous Solid Iron Substrate
- Estimation of Surface Tension of Molten Silicates Using Neural Network Computation
- Evaluation of the Surface Tension of Ternary Silicate Melts Containing Al_2O_3, CaO, FeO, MgO or MnO
- Fluid Flow and Free Surface Phenomena in Rotary Electromagnetic Stirring of a Metallic Melt
- A Model for Estimating Viscosities of Aluminosilicate Melts Containing Alkali Oxides
- Surface Tension Evaluation of Molten Silicates Containing Surface-active Components (B_2O_3, CaF_3 or Na_2O)
- Characteristics of Iron Entrainment into Slag Due to Rising Gas Bubbles
- Mechanisms of Iron Entrainment into Slag due to Rising Gas Bubbles
- Coupled Simulation of Heat Transfer and Phase Transformation in Continuous Casting of Steel
- Determination of Activities in Slags Containing Chromium Oxides.