Characterization of creep crack growth behaviour of 316 stainless steel in terms of microscopical fracture mechanism.
スポンサーリンク
概要
- 論文の詳細を見る
In order to understand the correlation between creep crack growth rate and microscopical fracture mechanism, creep crack growth tests were carried out using CT specimens on 316 stainless steel at various temperatures and stresses. Three kinds of fracture mechanisms, i.e., 1) wedge-type intergranular fracture (W-type), 2) transgranular fracture (T-type), 3) cavity-type intergranular fracture (C-type), were observed depending on testing conditions. Creep crack growth rate was evaluated by C* parameter. For a given C* value the creep crack growth rate in W- and C-type fracture modes was higher than that in T-type fracture mode. The relationship between creep crack growth rate and C* value for these fracture modes was discussed concerning creep properties, creep ductility and microscopical feature ahead of crack tip.
- The Iron and Steel Institute of Japanの論文
著者
-
Yagi Koichi
National Institute For Materials Science
-
Tabuchi Masaaki
National Inst. For Materials Science Independent Administrative Institution
-
Tabuchi Masaaki
National Research Institute For Metals
-
YAGI Koichi
National Research Institute for Metals
-
Ohba Toshio
National Research Institute for Metals
関連論文
- Creep Fracture Analysis of W Strengthened High Cr Steel Weldment
- Microstructural Investigations on Type IV Cracking in a High Cr Steel
- Materials solution for safe society
- Degradation of Creep Strength in Welded Joint of 9%Cr Steel
- Effects of Alloying Additions and Material Microstructure on the Accuracy of the Predictive Law of Creep Crack Growth for W-Strengthened 9-12%Cr Ferritic Heat-Resistant Steel
- The characterization of creep crack growth rate and its life of Cast TiAl-Fe-V-B Alloys(Strength & Fracture)
- Comparative Study of The Estimation of Creep Crack Growth Behaviour of TiAl by Using A Precrack And A Notch CT Specimens
- TTP Diagrams of Z Phase in 9-12% Cr Heat-Resistant Steels
- GS(6)-26(GSW0324) The Measurement and Estimation of Creep Crack Growth of a Round Bar Specimen with a Circular Notch for 12Cr Ferritic Heat Resistant Steel
- Analysis of Stress - Strain Relationship in Materials Containing Voids by Means of Plastic Finite Element Method
- Microstructures and Type-IV Creep Damage of High Cr Steel Welds
- The Influence of Both Testing Environment and Fillet Radius of the Die Holder on the Rupture Life of Small Punch Creep Tests
- 環境負荷低減を目指す材料開発 : エコマテリアル
- Characterization of creep crack growth behaviour of 316 stainless steel in terms of microscopical fracture mechanism.