Reconsideration on Al Coordination in CaO–SiO2–Al2O3–(R2O or RO) Glasses by Using High Field Solid-State 27Al NMR Spectroscopy
スポンサーリンク
概要
著者
-
Sukenaga Sohei
Department of Materials Science and Engineering, Kyushu University
-
Nagahisa Tetsuya
Department of Materials Science and Engineering, Kyushu University
-
Kanehashi Koji
Materials Characterization Research Lab., Advanced Technology Research Laboratories, Nippon Steel Co
-
Saito Noritaka
Department of Materials Science and Engineering, Kyushu University
-
Nakashima Kunihiko
Department of Materials Science and Engineering, Kyushu University
関連論文
- Reconsideration on Al Coordination in CaO–SiO2–Al2O3–(R2O or RO) Glasses by Using High Field Solid-State 27Al NMR Spectroscopy
- Viscosities of CaO-SiO_2-Al_2O_3-(R_2O or RO) Melts
- Influence of Slag Composition on Slag-Iron Interfacial Tension
- Recovery Rate of Chromium from Stainless Slag by Iron Melts
- Interfacial Tension between Molten Iron and CaO-SiO_2 Based Fluxes
- Wetting and Penetration Behavior of Calcium Ferrite Melts to Sintered Hematite
- Viscosity Measurement of Calcium Ferrite Based Slags during Structural Relaxation Process
- Penetration Behavior of Calcium Ferrite Melts into Hematite Substrate
- Glass-Metal Continuous Functionally Gradient Materials for Reflector Lamp
- Viscosity and Surface Tension Measurements of RE_2O_3-MgO-SiO_2 (RE=Y, Gd, Nd and La) Melts
- Formation Rate of Calcium Ferrite Melt Focusing on SiO_2 and Al_2O_3 Component
- Density and Surface Tension of CaO–SiO2–Al2O3–R2O (R=Li, Na, K) Melts
- Reconsideration on Al Coordination in CaO-SiO_2-Al_2O_3-(R_2O or RO) Glasses by Using High Field Solid-State ^Al NMR Spectroscopy
- Effect of Li_2O Addition on Crystallization Behavior of CaO-Al_2O_3-MgO Based Inclusions