水溶液プロセスを用いた鉄添加ハイドロキシアパタイトの合成
スポンサーリンク
概要
- 論文の詳細を見る
Development of non toxic magnetic beads has been strongly desired to cure more effectively for patients having diseases such as cancer and osteosarcoma. In this study, Fe doped calcium phosphate powders were prepared by aqueous solution process. The crystal phase of obtained samples had a hydroxyapatite (HAp)-related structure with low crystallinity, and the crystallinity of samples decreased with increasing ratio of Fe (RFe). The crystallinity of samples improved by heat treatment more than 1073 K for 2 hours and α-Fe2O3 phase was generated as a second phase. The lattice parameter of HAp phase drastically changed at RFe=1 mol% caused by the difference of ion radius between Ca ion and Fe ion, and there was a trend of that the a-axis shrinks and c-axis expands by further increment of RFe. The obtained powders had granular crystals with 10 nm in diameter. All samples showed paramagnetic property, and the maximum magnetization was 3×10-2 emu/g at RFe=5 mol%.
著者
関連論文
- 非晶質SiO2添加ハイドロキシアパタイトへの作製と評価
- 水溶液プロセスを用いた鉄添加ハイドロキシアパタイトの合成
- MOCVD法によるCa-Ti-OおよびCa-P-O系傾斜機能バイオセラミックス膜の合成
- 水溶液プロセスを用いた鉄添加ハイドロキシアパタイトの合成
- 非晶質SiO_2添加ハイドロキシアパタイトへの作製と評価
- Al2O3/Si3N4ナノコンポジット (脆性材料の評価)
- Al_2O_3-Sic複合材料の微細構造と機械的性質(セラミックスの微細構造)
- 323 アパタイトへのMg添加が及ぼす影響(生体材料,ナノ材料の創製と物性,オーガナイスドセッション8)
- 324 生体内での磁場駆動を目指したFe添加HApの合成と諸特性評価(生体材料,ナノ材料の創製と物性,オーガナイスドセッション8)
- 322 陽極酸化による新規酸化チタンの構造と特性(光触媒・生体機能,セラミック材料の創成と評価,オーガナイスドセッション8)
- 420 金属イオン添加水酸アパタイトの合成と評価(セラミック材料の合成プロセス,ナノ材料の創成と評価,オーガナイスドセッション8)