Solvothermal soft chemical synthesis and characterization of plate-like particles constructed from oriented BaTiO3 nanocrystals
スポンサーリンク
概要
- 論文の詳細を見る
Plate-like BaTiO3 particles with a size of about 200 nm in thickness and 3 μm in width were prepared by using a novel solvo-thermal soft chemical process in ethanol and water-ethanol mixed solvents. A layered titanate of H1.07Ti1.73O4 with a lepidocrocite-like structure and plate-like nanoparticle morphology was used as the precursor, and solvothermally treated in the Ba(OH)2 solution to prepare the BaTiO3 nanoparticles. The formation reaction, particle morphology, nanostructure, and crystal-axis-orientation of the plate-like BaTiO3 nanoparticles were studied by XRD, FE-SEM, and TEM. The plate-like BaTiO,3 nanoparticles are formed by an in situ topotactic structural transformation reaction. The crystallinity and particle morphology can be controlled by changing the fraction of ethanol in the solvent, Ba(OH)2 concentration, and reaction temperature. The plate-like BaTiO3 nanoparticles are polycrystalline particles constructed from spherical nanocrystals which are arranged in the same crystal-axis orientation in each plate-like particle, and show a high degree orientation in [110] direction, being suitable for preparing oriented BaTiO3 ceramic materials with high performance.
- 日本セラミックス協会の論文
著者
-
Feng Qi
Department Of Advanced Materials Science Faculty Of Engineering Kagawa University
-
Ishikawa Yoshie
Department of Advanced Materials Science, Faculty of Engineering, Kagawa University
-
Makita Yoji
National Institute of Advanced Industrial Science and Technology
-
Yamamoto Yuichi
Konoshima Chemical Co. Ltd.
関連論文
- Topotactic Preparation of Preferentially Oriented BaTiO_3 and TiO_2 Thin Films on Polycrystalline Substrate
- Hydrothermal Soft Chemical Synthesis of Ni(OH)_2-Birnessite Sandwich Layered Compound and Layered LiNi_Mn_O_2
- Solvothermal soft chemical synthesis and characterization of plate-like particles constructed from oriented BaTiO3 nanocrystals
- Transformation of layered hydroxide zinc benzoate nanosheets into ZnO nanocrystals by electron beam irradiation
- Synthesis of Manganese Oxide Nanofibers by Selfassembling Hydrothermal Process
- Synthesis and exfoliation of layered hydroxide zinc aminobenzoate compounds
- Preparation of Long Silver Nanowires from Silver Matrix by Electron Beam Irradiation
- Synthesis of a New Layered Manganese Oxide Nanocomposite through a Delamination/Reassembling Process
- Column Desulfurization from Hydrodesulfurization-Treated Gasoline Using Ce(IV)-Loaded Y-Zeolite Adsorbent
- Column Desulfurization of Hydrodesulfurized Gasoline Using Ce(IV)-Loaded Y-Zeolite Adsorbent
- Preparation of Nanoleaf-like Single Crystals of Anatase-type TiO_2 by Exfoliation and Hydrothermal Reactions
- Low Temperature Synthesis of BaTiO3 from Layered Titanate Nanosheet