A Fundamental Study on Static Strength Improvement of CFRP Bolted Joints by Increasing Friction Force
スポンサーリンク
概要
- 論文の詳細を見る
The bolted joint is a common assembling method for carbon fiber reinforced plastic (CFRP) members. However, cracks or plastic deformation can occur around bolt holes of CFRP members even when employing low fastening forces. As a result, CFRP failure occurs around bolt holes because of bearing forces, and the strength of a CFRP joint is reduced. To address this problem, we change the configurations of washers and insert a thin sheet having a high friction coefficient between CFRP members. In friction coefficient measurements, the insertion of sandpaper was found to be the most suitable method for increasing friction forces at the interface between CFRP members. Three-dimensional finite element method analyses were conducted to investigate the effect of washer configurations in terms of the maximum allowable fastening force and the joint strength. From these analyses, the cone washer was found to be the most effective design for increasing the joint strength. In the full model analyses, the failure strengths of proposed CFRP bolted joints were higher than those of normal CFRP bolted joints. The verification tests for the proposed joint were conducted according to ASTM D5961. It was observed that the load at failure for the proposed bolted joint was about 45 % greater than that for the conventional joint.
著者
-
Todoroki Akira
Department Of Mechanical Engineering And Science Tokyo Institute Of Technology
-
Mizutani Yoshihiro
Department of Materials Science and Engineering, Meijo University, Nagoya 468-8502, Japan
-
TODOROKI Akira
Department of Mechanical Engineering, Tokyo Institute of Technology
-
MATSUZAKI Ryosuke
Department of Mechanical Engineering, Tokyo Institute of Technology
-
KATSUMATA Tsukasa
Graduate School of Tokyo Institute of Technology
関連論文
- Transient and Dynamic Stress Analysis of Functionally Graded Thick Hollow Cylinder Subjected to Thermal Shock Loading Using an Analytical Method
- Fiber-waviness Model in Filament Winding Process
- Early Onset of Rhegmatogenous Retinal Detachment After LASIK with Femtosecond Laser
- A Fundamental Study on Static Strength Improvement of CFRP Bolted Joints by Increasing Friction Force
- Expanded Indications for 25-Gauge Transconjunctival Vitrectomy
- Twenty-gauge Transconjunctival Vitrectomy
- Surface Modification by Nanoimprint Lithography for Improvement of the Joint Strength of Composites
- A Novel Missense Mutation of Exon 3 in the Type A Human Natriuretic Peptide Receptor Gene: Possible Association with Essential Hypertension
- Haplotype-Based Case-Control Study of Estrogen Receptor α (ESR1) Gene and Pregnancy-Induced Hypertension
- Association Study Using Single Nucleotide Polymorphisms in the Estrogen Receptor β (ESR2) Gene for Preeclampsia
- Modified Gluteus Maximus V-Y Advancement Flap for Reconstruction of Perineal Defects After Resection of Intrapelvic Recurrent Rectal Cancer : Report of a Case
- Unsupervised Structural Damage Diagnosis Based on Change of Response Surface Using Statistical Tool : Application to Damage Detection of Composite Structure
- 114 Bearing Failure Detection of Bolted Composite Joints Using Electric Resistance Change Method
- Structural Health Monitoring : Sensors, Diagnostic Method and System
- Incubation Time of Stress Corrosion Cracking for Type 316L and Type 316 Stainless Steels by CBB Method in High Temperature Water
- Application of Electric Potential Method to Smart Composite Structures for Detecting Delamination
- Electrical Resistance Change of CFRP under a Compression Load
- Electrical Resistance Change of Thick CFRP Laminate for Self-Sensing
- Durability Estimates of Copper Plated Electrodes for Self-sensing CFRP Composites
- Mechanism of Electrical Resistance Change of a Thin CFRP Beam after Delamination Cracking
- Damage Monitoring for Semi-Transparent Composites Using Luminance of EL Backlight
- Detection of Matrix Crack Density of CFRP using an Electrical Potential Change Method with Multiple Probes
- Strain and Damage Monitoring of CFRP Laminates by Means of Electrical Resistance Measurement
- Stacking-Sequence Optimization of Composite Delta Wing to Improve Flutter Limit Using Fractal Branch and Bound Method
- Stacking sequence optimizations using modified global response surface in lamination parameters
- Fractal Property of Matrix Cracking in GFRP Cross-Ply Laminates
- Stacking Sequence Optimizations Using Fractal Branch and Bound Method for Laminated Composites
- Electrical Resistance Change of Unidirectional CFRP Due to Applied Load(Advanced Technology of Experimental Mechanics)
- Experimental Cost Reduction for Delamination Monitoring of CFRP Beam Using Electrical Resistance Change with Neural Networks(International Workshop on Smart Materials and Structural Systems, W03 Jointly organized by Material & Processing Division, Materia
- Optimizations of stacking sequence and number of plies for laminated cylinders using GA with intron genes
- Stacking sequence optimizations using GA with zoomed response surface on lamination parameters
- Application of Genetic Algorithms to Stiffness Optimization of Laminated Composite Plates with Stress-Concentrated Open Holes
- Two-Level Optimization of Dimensions and Stacking Sequences for Hat-Stiffened Composite Panel
- Low-Temperature Synthesis of Single-Walled Carbon Nanotubes in a High Vacuum Using Pt Catalyst in Alcohol Gas Source Method
- Numerical Simulation of Self-Sensing Time Domain Reflectometry for Damage Detection of Carbon Fiber Reinforced Polymer Plate
- Electrical Resistance Reduction of Laminated Carbon Fiber Reinforced Polymer by Dent Made by Indentation without Cracking
- Damage and Fault Diagnosis of In-service Structure via Statistical Comparison of Relation between Sensor measurements (Damage Diagnosis of in-service Structure under High Noise Environment using Multiple Reference Data):(Damage Diagnosis of in-service St
- Damage Monitoring of CFRP Plate Using Self-Sensing TDR Method
- Numerical method for solving steady three-dimensional heat conduction problem in sector column.