Damage Monitoring for Semi-Transparent Composites Using Luminance of EL Backlight
スポンサーリンク
概要
- 論文の詳細を見る
The present paper a new damage monitoring system that employs luminance of EL backlight for semi-transparent composites. For the semi-transparent composites, damage is easily found by visual inspections. In the cases that the structures are sealed or huge structures, however, the visual inspections are difficult. The present paper adopts a system using change of luminance of transmitted light. When the composite structures are damaged, the damage reduces luminance of the transmitted light from the backside. The present study adopts an Electro Luminescent device (EL) as the backlight. The EL device can emit uniform-plane-light and is a very flexible device. The EL device can be mounted on a curved surface. Fatigue tests are conducted using rectangular specimens with an open hole fabricated from fabric glass/epoxy composites. The monitoring system is applied to the fatigue tests, and it is experimentally shown that the method can detect the fatigue damage without loading.
- 2000-01-15
著者
-
Todoroki Akira
Department Of Mechanical Engineering And Science Tokyo Institute Of Technology
-
Shimamura Yoshinobu
Department Of Mechanical Engineering And Science Tokyo Institute Of Technology
-
Shimamura Yoshinobu
Department Of Mechano-aerospace Engineering Tokyo Institute Of Technology
関連論文
- Transient and Dynamic Stress Analysis of Functionally Graded Thick Hollow Cylinder Subjected to Thermal Shock Loading Using an Analytical Method
- Fiber-waviness Model in Filament Winding Process
- A Fundamental Study on Static Strength Improvement of CFRP Bolted Joints by Increasing Friction Force
- Quantitative Dependence of the Effective Modulus of Particle Reinforced Composites on Partially Debonding Damage
- Unsupervised Structural Damage Diagnosis Based on Change of Response Surface Using Statistical Tool : Application to Damage Detection of Composite Structure
- Delamination Identification in Composite Laminates by Anti-Resonant Frequency
- 114 Bearing Failure Detection of Bolted Composite Joints Using Electric Resistance Change Method
- Structural Health Monitoring : Sensors, Diagnostic Method and System
- Application of Electric Potential Method to Smart Composite Structures for Detecting Delamination
- Electrical Resistance Change of CFRP under a Compression Load
- Electrical Resistance Change of Thick CFRP Laminate for Self-Sensing
- Durability Estimates of Copper Plated Electrodes for Self-sensing CFRP Composites
- Mechanism of Electrical Resistance Change of a Thin CFRP Beam after Delamination Cracking
- Damage Monitoring for Semi-Transparent Composites Using Luminance of EL Backlight
- Detection of Matrix Crack Density of CFRP using an Electrical Potential Change Method with Multiple Probes
- Strain and Damage Monitoring of CFRP Laminates by Means of Electrical Resistance Measurement
- Stacking-Sequence Optimization of Composite Delta Wing to Improve Flutter Limit Using Fractal Branch and Bound Method
- Stacking sequence optimizations using modified global response surface in lamination parameters
- Fractal Property of Matrix Cracking in GFRP Cross-Ply Laminates
- Stacking Sequence Optimizations Using Fractal Branch and Bound Method for Laminated Composites
- Electrical Resistance Change of Unidirectional CFRP Due to Applied Load(Advanced Technology of Experimental Mechanics)
- Experimental Cost Reduction for Delamination Monitoring of CFRP Beam Using Electrical Resistance Change with Neural Networks(International Workshop on Smart Materials and Structural Systems, W03 Jointly organized by Material & Processing Division, Materia
- Optimizations of stacking sequence and number of plies for laminated cylinders using GA with intron genes
- Stacking sequence optimizations using GA with zoomed response surface on lamination parameters
- Application of Genetic Algorithms to Stiffness Optimization of Laminated Composite Plates with Stress-Concentrated Open Holes
- Two-Level Optimization of Dimensions and Stacking Sequences for Hat-Stiffened Composite Panel
- Fracture Mechanics Study on Stress Corrosion Cracking Behavior under Corrosive Environment
- Numerical Simulation of Self-Sensing Time Domain Reflectometry for Damage Detection of Carbon Fiber Reinforced Polymer Plate
- Electrical Resistance Reduction of Laminated Carbon Fiber Reinforced Polymer by Dent Made by Indentation without Cracking
- Damage and Fault Diagnosis of In-service Structure via Statistical Comparison of Relation between Sensor measurements (Damage Diagnosis of in-service Structure under High Noise Environment using Multiple Reference Data):(Damage Diagnosis of in-service St
- Monte Carlo Simulation of Stress Corrosion Cracking on Smooth Surface of a Sensitized Stainless Steel Type 304 under Non-Uniform Stress Condition
- Damage Monitoring of CFRP Plate Using Self-Sensing TDR Method