燃焼合成を利用したTiC/Ti, TiB_2/Ti傾斜機能材料の作製
スポンサーリンク
概要
- 論文の詳細を見る
The most difficult task of fabrication of ceramics-metal functionally gradient materials (FGMs) by the powder molding method is to simultaneously sinter two materials with largely different sintering temperature. In this work, the mixed powders of Ti and C and Ti and B were laminated with gradually changing composition, and then sintered using self-propagating high-temperature synthesis (SHS). It was found that TiC/Ti and TiB2/Ti FGMs with high hardness could be fabricated from two kinds of the mixed powders at the lower sintering temperature than that of monolithic TiC and TiB2. Two kinds of FGMs were fabricated by spark plasma sintering(SPS) and pressureless sintering.
- 2006-02-15
著者
関連論文
- 燃焼合成を利用したTiC/Ti, TiB_2/Ti傾斜機能材料の作製
- 6061-T6アルミニウム合金摩擦攪拌接合継手の疲労挙動
- 粉体押出成形によるMg-Zr合金の創製と機械的特性
- マグネシウム合金の押出加工による結晶粒微細化と疲労強度の改善
- マグネシウム合金の疲労挙動に及ぼす押出条件の影響(S14-3 軽金属・軽量金属・細線の疲労,S14 金属材料の疲労特性と破壊機構)
- 粉体押出成形によるマグネシウム合金の機械的特性の改善
- 新プレス加工方式によるアンダーカット成形
- 501 Mg_2Si粒子強化Mg合金の疲労挙動と破壊機構(OS2-1,OS2 各種機械材料の疲労挙動と強度評価)
- P3 マグネシウム合金AZ61AおよびAZ80押出材の疲労挙動に及ぼす押出比の影響(疲労,ポスター講演3)
- 1311 固相合成法によるMg_2Si分散マグネシウム合金の疲労挙動(S21-1 軽金属の疲労,S21 金属材料の疲労特性と破壊機構)
- マグネシウム合金AZ61押出し材の疲労挙動と破壊機構(GS3 疲労・Mg合金・Ti合金)
- 411 マグネシウム合金 AZ31 圧延材の疲労挙動と破壊機構
- マグネシウム合金 AZ31 圧延材の疲労き裂進展特性
- 311 マグネシウム合金 AZ31 圧延材の疲労き裂進展特性