Preparation of nano-crystalline MFI zeolite via hydrothermal synthesis in water/surfactant/organic solvent using fumed silica as the Si source
スポンサーリンク
概要
- 論文の詳細を見る
The preparation of nano-crystalline MFI zeolites (Silicalite-1 and ZSM-5) was carried out by hydrothermal synthesis in a water/surfactant/organic solvent using fumed silica and aluminum sulfate as the Si and Al source, respectively. It was confirmed that the surfactant in the solution affected the nucleation rate of the MFI zeolite. Moreover, the crystal size of the MFI zeolite decreased with increasing surfactant concentration, and nanometer-sized MFI zeolites was obtained at a surfactant concentration of 0.25～0.5 mol/L. The successful preparation of MFI zeolite nanocrystals was ascribed to the stabilization of the MFI zeolite precursors and/or crystals by the adsorbed surfactant on their surface. This method was applied to the preparation of nano-crystalline ZSM-5 zeolite. ZSM-5 zeolite with a crystal size of approximately 50 nm was obtained. The nano-crystalline ZSM-5 zeolite was well-crystallized without octahedral Al atoms in the external framework, and exhibited almost the same acidity as a reference ZSM-5 zeolite.
著者
関連論文
- Preparation of nano-crystalline MFI zeolite via hydrothermal synthesis in water/surfactant/organic solvent using fumed silica as the Si source
- Effects of the Affinity between the Pore Wall and Solvent on the Intracrystalline Diffusivities of Benzene within Porous Materials in the Liquid Phase
- Preparation of hydrophilic silicalite-1 nanocrystal-layered membranes and their application to separating water from water–acetone solution
- Recovery of Ammonia from Biomass Waste by Adsorption on Magnesium Phosphate Derived from Magnesium Ammonium Phosphate
- Recovery of Useful Chemicals from Paper Sludge-Derived Tar by Catalytic Partial Oxidization over Zirconia-Supporting Iron Oxide Catalysts in Steam Atmosphere
- Recovery of Lighter Fuels from Petroleum Residual Oil by Oxidative Cracking with Steam over Zr-Al-FeO_x Catalyst
- Selective synthesis for light olefins from acetone over ZSM-5 zeolites with nano- and macro-crystal sizes
- New Method for Preparing Monodispersed Nanocrystalline Silicalite via Hydrothermal Synthesis in Water/Surfactant/Oil Solution
- Control of Acid-Site Location of MFI Zeolite by Catalytic Cracking of Silane and Its Application to Olefin Synthesis from Acetone
- Kinetics of n-hexane cracking over ZSM-5 zeolites : Effect of crystal size on effectiveness factor and catalyst lifetime