Recovery of Ammonia from Biomass Waste by Adsorption on Magnesium Phosphate Derived from Magnesium Ammonium Phosphate
スポンサーリンク
概要
- 論文の詳細を見る
Ammonia in animal wastes causes eutrophication of the soil when these wastes are used as liquid fertilizer. Accordingly, it is desirable to recover ammonia from these wastes. We investigate the following two methods for recovery of ammonia: (i) recovery of gaseous ammonia, which was generated by aeration of the ammonia gas, by adsorption on the magnesium phosphate adsorbent derived from magnesium ammonium phosphate (MAP); and (ii) recovery of aqueous ammonium ions by adsorption on the same adsorbent. The adsorbent was prepared by treatment of MAP at 378 K, and the XRD pattern of the adsorbent shows that MAP structure disappeared after the treatment. Gaseous ammonia and aqueous ammonium ions were adsorbed on the adsorbents, and the amounts of ammonium ions adsorbed were larger than that of gaseous ammonia. The adsorption isotherms of aqueous ammonium ions and gaseous ammonia exhibited Langmuir- and Henry-type characteristics, respectively, indicating different adsorption mechanism between aqueous ammonium ions and gaseous ammonia. It was found that MAP structure was re-formed in the presence of water after the aqueous ammonium ions adsorption, while the structure of the adsorbent had hardly changed after the gaseous ammonia adsorption. The low adsorption energy (–3.0 kJ/mol) of gaseous ammonia indicates that physical adsorption. Consequently, adsorption of aqueous ammonium ions is a suitable method for recovery large amounts of ammonia, and we demonstrate that large amounts of ammonium ions are recovered from cow urine after hydrothermal treatment of it.
- 社団法人 化学工学会の論文
- 2009-03-01
著者
-
Masuda Takao
Division Of Chemical Process Engineering Graduate School Of Engineering Hokkaido University
-
Tago Teruoki
Division Of Chemical Process Engineering Graduate School Of Engineering Hokkaido University
-
FUMOTO Eri
Energy Technology Research Institute, National Institute of Advanced Industrial Science and Technolo
-
Fumoto Eri
Energy Technology Research Institute National Institute Of Advanced Industrial Science And Technolog
関連論文
- Preparation of nano-crystalline MFI zeolite via hydrothermal synthesis in water/surfactant/organic solvent using fumed silica as the Si source
- Effects of the Affinity between the Pore Wall and Solvent on the Intracrystalline Diffusivities of Benzene within Porous Materials in the Liquid Phase
- Preparation of hydrophilic silicalite-1 nanocrystal-layered membranes and their application to separating water from water–acetone solution
- Recovery of Ammonia from Biomass Waste by Adsorption on Magnesium Phosphate Derived from Magnesium Ammonium Phosphate
- Recovery of Useful Chemicals from Paper Sludge-Derived Tar by Catalytic Partial Oxidization over Zirconia-Supporting Iron Oxide Catalysts in Steam Atmosphere
- Recovery of Lighter Fuels from Petroleum Residual Oil by Oxidative Cracking with Steam over Zr-Al-FeO_x Catalyst
- Steam Reforming of Oils Produced from Waste Plastics
- Selective synthesis for light olefins from acetone over ZSM-5 zeolites with nano- and macro-crystal sizes
- New Method for Preparing Monodispersed Nanocrystalline Silicalite via Hydrothermal Synthesis in Water/Surfactant/Oil Solution
- Control of Acid-Site Location of MFI Zeolite by Catalytic Cracking of Silane and Its Application to Olefin Synthesis from Acetone
- Kinetics of n-hexane cracking over ZSM-5 zeolites : Effect of crystal size on effectiveness factor and catalyst lifetime