酸化物分散強化白金合金の高温疲労破壊
スポンサーリンク
概要
- 論文の詳細を見る
High temperature fatigue of oxide-dispersion-strengthened (ODS) platinum alloys was investigated at 1673 K and 1473 K in air. ODS platinum alloys used in this study were composed of sintered Pt-10 mass% Rh (Pt-10%Rh) alloy matrix and dispersed zirconia particles. Fatigue tests were conducted in the tension-tension cyclic mode with the R-ratio value of 0.1. Fatigue fracture surface of the ODS alloys showed clear difference from those of conventional Pt-10%Rh alloys. The fatigue strength of the ODS alloys at high temperatures were about three times higher than that of the Pt-10%Rh alloys. The fatigue rupture time of the ODS alloys was comparable to creep rupture time under a condition of maximal stress, while the fatigue rupture time of Pt-10Rh alloys is comparable to creep rupture time under a condition of average stress.
論文 | ランダム
- 現代日本国家論の方法 : R・スティーヴンの階級分析によせて
- ネオ・コーポラティズム討論について : ネオ・マルクス主義国家論からの覚え書
- 「政治」イメージの政治学 : マルクス主義的アプローチの場合
- コミンテルンの日本像(一九二九 -三一年) : 「世界綱領」と「三一年政治テーゼ草案」
- I-37. 重症胃出血手術例の検討(第2回日本消化器外科学会大会)