NiAl-X合金/酸化皮膜界面の微細構造に及ぼす添加元素の影響
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify spalling mechanism of oxide scale on NiAl, microstructures in the vicinity of NiAl-X(Hf, Zr)/oxide scale interfaces were observed by using TEM. The oxidation tests were done at 1373 K in air for up to 360 ks. In NiAl, many voids were formed at the substrate/Al2O3 interface, leading to spalling of the alumina scale. On the other hand, addition of Hf or Zr to NiAl leads to suppression of the void formation, resulting in prevention of spalling of alumina scale. In addition, a Ni-Al-O layer tends to be formed at the interface in NiAl. This demonstrates appreciable increase in oxygen partial pressure and nickel activity at the interface. In fact, GDS measurements indicated depression of the Al concentration in the substrate close to an alumina scale. Consequently, it was speculated that the addition of Hf or Zr leads to increase in diffusivity of Al in the substrate and suppression of void formation at NiAl/alumina scale, resulting in prevention of spalling of an alumina scale.
- 社団法人 高温学会 (High Temperature Society of Japan)の論文
著者
関連論文
- Mo-Si系金属間化合物基超高温耐熱材料の合金設計と組織制御
- Bを添加したWSi_2焼結体の組織と高温酸化挙動
- 金属間化合物中の過飽和熱空孔の自己組織化と機械的性質への影響(OS11f 材料の組織・強度に関するマルチスケールアナリシス)
- 2009年北海道夏期セミナー報告
- 2009年北海道夏期セミナー報告
- 2008年北海道夏期セミナー報告 : 主題 : 環境にやさしい表面処理技術
- 2007年北海道夏期セミナー報告 : 主題 : 自動車産業と表面技術
- β-Ni(Al,Cr)合金に形成されるAl2O3酸化皮膜の耐剥離性に及ぼすZr添加の影響
- Cr_2O_3皮膜の劣化に及ぼす水蒸気の影響
- 水蒸気含有雰囲気においてAl-Mg合金に形成される高温酸化皮膜
- 水蒸気含有雰囲気におけるB添加WSi2の酸化挙動
- 鉛フリーはんだ溶湯中における炭素鋼の溶食挙動
- 配管と材料 Cr-Si-Ni系材料の耐高温腐食性皮膜への応用
- NiAl-X合金/酸化皮膜界面の微細構造に及ぼす添加元素の影響
- 酸化雰囲気におけるCrSi2溶射膜/炭素鋼界面の反応
- 放電プラズマ焼結したCrSi2の高温酸化挙動
- 貝殻の組織を材料学的視点で観察すると (特集 第5回21世紀の境界領域研究を考えるシンポジウム)
- ステンレス鋼の高温酸化に及ぼす水蒸気の役割
- 1473Kの水蒸気含有雰囲気におけるSUS430ステンレス鋼の高温酸化
- SAC/Cu界面反応層構造に及ぼすNi添加の影響
- Sn-低Bi合金の組織と硬さの関係
- 鉄基合金の溶食挙動に及ぼす合金元素の影響
- Snのsub-grainの形成に及ぼす添加元素の影響
- 2007年北海道夏期セミナー報告 : テーマ : 自動車産業と表面技術
- 2010年北海道夏期セミナー並びに北海道支部設立20周年記念式典・記念講演の報告
- NiAl-X合金/酸化皮膜界面の微細構造に及ぼす添加元素の影響
- 化学系学協会北海道支部2011年冬季研究発表会報告