20. スチレン重合に対する超音波周波数効果
スポンサーリンク
概要
- 論文の詳細を見る
Effect of Ultrasound on polymerization of polystyrene was studied at the frequency of 45.7kHz. All the experiments were carried out under N_2 atmosphere at 50℃. The ultrasonic intensity was estimated using the chemical dosimeter based on the decomposition of porphyrin. The average-weight molecular weights were evaluated by the gel permeation chromatograph. The yield of polystyrene increased with increasing the sonication time. After the sonication was stopped, the termination of polymerization was observed. However, when the ultrasound was irradiated into the reaction vessel again, the polymerization set in. The average-weight molecular weight decreased with increasing the sonication time. After longer sonication it approached the limiting value.
- 日本ソノケミストリー学会の論文
著者
関連論文
- P1-B-14 弾性表面波によるガラス基板上の高分子薄膜の物性評価(超音波物性・材料,ポスターセッション1(概要講演))
- P2-14 高分子複合材料の音波物性に及ぼす無機充填材の効果(ポスターセッション2,ポスター発表)
- PA18 表面波測定によるPAAゲルの物性評価(基礎・物性,ポスターセッション2)
- PA6 過冷却状態におけるテトラエチレングリコールの局所構造と構造緩和との相関(ポスターセッション2)
- PG9 超音波分解反応に対する反応容器体積の影響(ポスターセッション2)
- 21. シングルバブルソノルミネッセンスに対するアルコール添加効果(21)
- P2 単一気泡による化学作用の研究(ソノケミストリーの基礎科学)
- P16 円筒型超音波反応器のソノケミカル反応効率
- 21. シングルバブルによる化学作用 : 亜硝酸の生成反応
- 17. スチレンリビングラジカル重合に対する超音波照射効果の検討
- P-25 サーモグラフィーによる円筒型超音波反応器の評価(ポスターセッション)
- 3. フェノールフタレインを用いた超音波強度の簡易測定法の検討
- 20. スチレン重合に対する超音波周波数効果
- 22. 超音波照射時の水に対する溶存気体の影響