OS0523 析出強化型ステンレス鋼A286の疲労特性に及ぼす硬さの分布の影響(OS5-5 寿命予測,OS-5 材料の疲労挙動と損傷評価2)

概要

論文の詳細を見る
In order to clarify the relationship between fatigue strength and hardness of precipitation strengthening type stainless steel: A286, tensile tests, fatigue tests and Vickers hardness tests were performed. As a result of the tests, A286 steel have high tensile strength as well as low fatigue strength. Then, from the result of hardness test, there is large variability in hardness distribution of A286 steel. High hard zone and low hard zone were found in a specimen of A286 steel. The hardness of the zone in which many cracks initiated, is lower than the zone in which few cracks initiated. It is considered that high tensile strength is based on average both high hardness zone and low hardness zone when tensile test, and low fatigue strength was caused by the fatigue cracks which are easy to initiate and propagate in low hardness zone. Therefore, this is the reason why the fatigue strength ratio of A286 steel is lower than most steel.
一般社団法人日本機械学会の論文
2011-07-16