This paper presents effects of injected seawater on decommissioning process of the Fukushima I nuclear power plant and problems of electric power associated with nuclear power plants. First, stress corrosion cracking (SCC) test of welding stainless steel was performed in solution water of NaCl during one month. As the results, though the corrosion was found at welded heat-affected zone in the specimen, SCC could not be found. We forecast that decommissioning of the nuclear power plant is hard because initiation probability of SCC becomes extremely-high with the course of long time. Second, we carried out questionnaire study which asked students their attitudes towards needs of nuclear power plants and safety of disengaged that. From the questionnaire results, they pretty understood the risk of nuclear power plants, but needed nuclear power plants for avoiding electric power shortage.
- 2013-01-31
著者
関連論文
- 損傷許容型先進セラミックス材料の球押込みによるリングクラック発生強度分布特性
- 多孔質セラミックスのリラクゼーション試験
- 脆性固体のSCG 破壊と遷移確率
- 脆性固体の各種負荷様式下でのSCG 破壊モデリング
- ぜい性材料の変動負荷速度下での確率論的強度評価
- 熱活性化過程に基づく統一的時間依存型破壊モデルと多孔質セラミックスの破壊強度特性
- セラミックスのための熱衝撃後の残存強度予測
- G0300-1-1 変動負荷速度下における脆性材料の破壊強度評価のための確率論的アプローチ([G0300-1]材料力学部門一般講演(1):破壊)
- 611 脆性固体の2段負荷速度下における確率論的破壊強度挙動(GS 材力・材料1)
- 多孔質セラミックスの曲げ強度に及ぼす寸法効果と負荷速度依存性
- 超塑性2相(α+γ)ステンレスの固相接合に及ぼす加熱温度と接合時間の影響
- セラミックスに対する確率論的等疲労寿命線図
- ステンレス鋼の応力腐食割れと原発問題に関する一考察
- 液晶ディスプレイを利用した光弾性による引張負荷を受けたポリカーボネートの応力可視化-体験入学でのデモンストレーション-
- ミニ研究の導入に向けた取り組み
- 静荷重を受けたモノリシックセラミックスの残存強度特性
- 9-106 沼津高専におけるミニ研究の導入((04)工学教育の個性化・活性化-I)
- 9-226 メカトロダーツ競技会を通じた低学年工学基礎実験におけるPBL教育((04)工学教育の個性化・活性化-V/(13)教育評価・自己点検・評価システム-I)
- S042022 変動負荷速度下におけるセラミックスの動的疲労強度分布特性と破壊メカニズム([S04202]セラミックスおよびセラミックス系複合材料(2))
- 空気中における超塑性アルミニウム合金の固相接合