マイクロエマルション法による二酸化マンガンの合成と電池性能
スポンサーリンク
概要
- 論文の詳細を見る
The manganese dioxide power was synthesized by microemultion method, Potassium permanganate aqueous solution was dispersed in isooctane by bis (2-ethyhexyl) sulfosuccinate sodium (AOT) as the surfactant. Then potassium permanganate was reduced by AOT to produce manganese dioxide. The formation of α-MmO[2] phase was confirmed by X-ray diffraction after acidic leaching treatment and heating at 375℃ for 3h in air. The particle sizes were30-100nm and the specific surface areas were 139-150m[2]g[-1]. The Mn (IV) contents of the products (72-76%) were lower than that of electrolytic manganese dioxide (EMD, 93%). When the product was used as the cathode material of lithium / manganese ozide cell, the highset discharge capacity at 0.88 mA cm[-2] was 183 mAhg[-1], which higher than that of the cell using electrolytic manganese dioxide (176 mAhg[-1]).
- 2011-10-31
著者
関連論文
- 硝酸マンガンおよび硫酸マンガンからのLiMn_2O_4の合成とその放電特性
- 過マンガン酸塩と硫酸マンガンからのリチウム一次電池用二酸化マンガンの合成
- 硝酸マンガン溶液のオゾン酸化からのリチウム一次電池用二酸化マンガンの合成
- 酢酸マンガンとペルオキソ二硫酸アンモニウムからのリチウム一次電池用二酸化マンガンの合成
- 二価マンガン塩と硝酸アンモニウムからの二酸化マンガンの合成
- 噴霧熱分解法によるリチウム一次電池用二酸化マンガンの合成
- ゾルーゲル法によるリチウム一次電池用二酸化マンガンの合成
- カルバメート法によるMnCO_3からのフェライト原料としての重質Mn_3O_4の合成
- 大牟田・荒尾地域の大気汚染
- 重質化CMDを用いたリチウム2次電池用正極活物質の合成とその特性-2-CMD-LiOH加熱処理物を正極活物質として用いたリチウム2次電池特性
- クロレ-ト反応によるCMDの重質化処理とその生成物の物性
- Mn-NH4-カルバメ-トからのCMDの合成とその特性に関する研究-4-重質化CMDの加熱特性とその脱水物のLi-Mn電池への適応性について〔英文〕
- 炭酸マンガンと各種リチウム化合物との加熱処理によるリチウム2次電池用正極活物質の合成
- 炭酸マンガン加熱物の酸処理によるリチウム一次電池用二酸化マンガンの合成
- マイクロエマルション法による二酸化マンガンの合成と電池性能
- 過マンガン酸塩の還元反応による微粒子二酸化マンガンの合成と電池性能