概要
- 論文の詳細を見る
Manganese dioxides were prepared by acidic leaching treatment (nitric acid solution at 50℃ for 24h) of manganese carbonate heated at 550℃. The formation of γ-MnO[2] phase was confirmed by X-ray diffraction. After heating at 375℃ for 3h in air, the formation of β-MnO[2] phase was observed. The Mn(IV) contents and specific surface area of the product were 96% and 59m[2] g[-1], respectively. The powders were in a range of 0.2-1 μm. When the product was used as the cathode material of lithium / manganese oxide cell, the discharge capacity at 0.88 mA cm[-2] was 281 mAh g[-1], which were higher than that of the cell using electrolytic manganese dioxide (178 mAh g[-1]). It was found that the product obtained by this process is hopeful to be used as a cathode material.
- 2009-10-30
著者
関連論文
- 硝酸マンガンおよび硫酸マンガンからのLiMn_2O_4の合成とその放電特性
- 過マンガン酸塩と硫酸マンガンからのリチウム一次電池用二酸化マンガンの合成
- 硝酸マンガン溶液のオゾン酸化からのリチウム一次電池用二酸化マンガンの合成
- 酢酸マンガンとペルオキソ二硫酸アンモニウムからのリチウム一次電池用二酸化マンガンの合成
- 二価マンガン塩と硝酸アンモニウムからの二酸化マンガンの合成
- 噴霧熱分解法によるリチウム一次電池用二酸化マンガンの合成
- ゾルーゲル法によるリチウム一次電池用二酸化マンガンの合成
- カルバメート法によるMnCO_3からのフェライト原料としての重質Mn_3O_4の合成
- 大牟田・荒尾地域の大気汚染
- 重質化CMDを用いたリチウム2次電池用正極活物質の合成とその特性-2-CMD-LiOH加熱処理物を正極活物質として用いたリチウム2次電池特性
- クロレ-ト反応によるCMDの重質化処理とその生成物の物性
- Mn-NH4-カルバメ-トからのCMDの合成とその特性に関する研究-4-重質化CMDの加熱特性とその脱水物のLi-Mn電池への適応性について〔英文〕
- 炭酸マンガンと各種リチウム化合物との加熱処理によるリチウム2次電池用正極活物質の合成
- 炭酸マンガン加熱物の酸処理によるリチウム一次電池用二酸化マンガンの合成
- マイクロエマルション法による二酸化マンガンの合成と電池性能
- 過マンガン酸塩の還元反応による微粒子二酸化マンガンの合成と電池性能