142 活性金属ろうを用いたC/C複合材料とチタン合金との異材間ろう付(溶接・接合のプロセスと評価)
スポンサーリンク
概要
- 論文の詳細を見る
Carbon-carbon composites were brazed to a pure titanium using a Ag-Cu-Ti filler metal (Cusil-ABA^<[○!R]>) at 830℃ for 60s or 300s in vacuum of 1.0×10^<-4> Torr. The microstructure of the brazed joint interface was observed through the optical microscope and the scanning electron microscope (SEM). By analyzing with the energy dispersive spectroscopy (EDS), the constituents' distribution at the brazed interface was measured. Those observations and analyses revealed that the yarns of C/C composites were disbanded into the carbon fibers, and that the carbon fibers were corroded. The titanium included not only in the brazing filler metal but also in the bulk metal which diffused into the molten brazing filler metal formed the carbide to corrode the C/C composites. The corrosion was more severe for the brazed joint made by a longer brazing time. These results suggest that the brazing time must be shorter to obtain the stronger brazed joint for C/C composites and titanium.
- 一般社団法人日本機械学会の論文
- 2009-11-06
著者
関連論文
- アルミニウム合金とステンレス鋼の大気中ろう付用フラックスの研究
- C/C複合材料と純チタンのろう付に及ぼす積層方向の影響
- ロケットノズルスカートアッシィ用四管束試験片ろう付継手部の強度と接合部間隙の関係
- A-TIGによるSUS316L溶接部の組織と水素透過後の影響
- 348 配管用鋼管の高周波ろう付圧接におけるフィレットの形成と効果
- 414 鋼管の高周波ろう付圧接に関する研究
- 超音波を併用したダイヤモンドのFe - 42NiへのZn - 5Alはんだ付
- Pd薄膜とステンレス鋼の拡散接合
- 445 活性金属ろうを用いたC/C複合材料とチタンとの異材間ろう付(マイクロ接合(I),平成20年度秋季全国大会)
- 242 SUS304ステンレス鋼溶接部における水素透過経路の探査(溶接冶金(VI),平成20年度秋季全国大会)