ハイドロタルサイト様化合物を用いたリン除去 : 医薬・環境技術分野への応用に関して(<シンポジウム特集>層状複水酸化物の応用-陰イオン交換特性の利用-)

スポンサーリンク

概要

• 論文の詳細を見る

• A Cl^- intercalated hydrotalcite-like compound (Cl/LDH) was prepared by neutralizing magnesium and aluminum chlorides with sodium hydroxide. A Cl^- ions in the interlayer of Cl/LDH can be exchanged with phosphate equivalently. The isotherm for phosphate uptake followed the Langmuir equation at pH 7.53 and 310K: it gave an ion-exchange capacity of 2.37mmol of P/g for phosphate. The process of phosphate/Cl^- ion exchange could be divided into three stages depending on the amount (P_<load>) of phosphate loading. In stage I (0%<P_<load><6%), the Cl^--intercalated phase (interlayer distance =0.30nm) alone was observed. In stage II (6%<P_<load><80%), the phase transition from the Cl^--intercalated phase to the phosphate-exchanged phase (interlayer distance =0.36nm) took place. In stage III (80%<P_<load><100%), the phosphate-exchanged phase alone was observed; the interlayer distance increased slightly (from 0.36 to 0.37nm) with an increase in the phosphate loading, indicating a formation of solid solution. The phosphate/Cl^- ion-exchange reaction with Cl/LDH was not affected by the presence of trypsin. On the other hand, the trypsin adsorption was significantly depressed by the loading of phosphate. In the removal of phosphate from brackish river water using Cl/LDH, Kawamoto et al. indicated that phosphorous concentrations in the river water went up from 0.1mg P dm^<-3> to 0.02mg P dm^<-3> under the condition of a column method with a space velocity of 5.0hr^<-1>. The value of 0.02mg P dm^<-3> was considered to be enough for the repression of algae growth. As a zero-emission type phosphorous removal system, Oshima et al. suggested that two-step regeneration system, which uses a NaOH-NaCl mixed aqueous solution as the desorbing solution and a MgCl_2 aqueous solution as the regenerating solution. Moreover, phosphate ions can be recovered as magnesium ammonium phosphate (MAP) from the desorbing solution in the system.

• 2011-03-30

著者

• 大久保 彰

  富田製薬株式会社

• 大久保 彰

  富田製薬株式会社研究開発部

関連論文

• ハイドロタルサイト担持繊維(HTCF)のリン吸着能力・再生特性
• B8.リン酸イオン高選択性無機イオン交換体を用いた排水からのリン回収 : 効率的かつ経済的な再資源化方法について(一般講演 口頭発表,第50回粘土科学討論会発表論文抄録)
• B8 リン酸イオン高選択性無機イオン交換体を用いた排水からのリン回収 : 効率的かつ経済的な再資源化方法について
• B19. 層状化合物の環境浄化への応用 : 水環境からのリン除去(第48回粘土科学討論会発表論文抄録)
• 銅導入型および亜鉛導入型合成ハイドロタルサイトによるリン除去
• リン酸イオン高選択性無機層状イオン交換体を用いた排水からのリン除去
• リン酸イオン高選択性Mg-Al-Cl型ハイドロタルサイト'TPEX'を用いた浄化槽処理水からのリン除去
• S07 ハイドロタルサイト様化合物を用いたリン除去 : 医薬・環境技術分野への応用に関して(層状複水酸化物の応用-陰イオン交換特性の利用-,シンポジウム)
• ベーマイトを用いた醤油中のリン酸イオンの除去
• ハイドロタルサイト様化合物を用いたリン除去 : 医薬・環境技術分野への応用に関して(層状複水酸化物の応用-陰イオン交換特性の利用-)

スポンサーリンク