調理用電子レンジで焼結した部分安定化ジルコニアの微細構造と強度
スポンサーリンク
概要
- 論文の詳細を見る
Partially stabilized zirconia (PSZ) powders were fully densified by microwave heating using a microwave oven. Thepressed powder compacts of PSZ were sandwiched between two ZnO-MnO2-Al2O3 (ZMA)ceramic plates acting aspre-heaters in the microwave oven and put in the oven. PSZ ceramics fabricated with the microwave oven for 16 minexhibited a density of 5.94 g/cm3, which is approximately equal to the density of bodies sintered at 1350℃ for 4 h or at1400℃ for 16 min by the conventional furnace method. The PSZ pellet pre-heated by the ZMA ceramics more easilyabsorbed the microwave energy and self-heated to a higher temperature. The microwave heating enhanced not onlythe densification but also the grain growth. The mechanical strength of PSZ sintered by a microwave oven showed 900MPa in maximum.
- 2010-07-14
著者
関連論文
- 調理用電子レンジで焼結した部分安定化ジルコニアの微細構造と強度
- 2F04 C 軸配向性透明 ZnO 多結晶を基板とした p-SrCu_2O_2/n-ZnO P-N ヘテロ接合紫色発光ダイオードの作製
- 配向性酸化亜鉛における電気伝導性の測定
- 酸化亜鉛焼結体のガスセンサー特性
- 酸化亜鉛ガスセンサー上の酸素吸着に対する白金担持効果
- 半導体化多孔質チタン酸バリウムの吸着酸素とPTCR効果
- ZnOバリスターにおける酸素の促進拡散
- 固体電解質 (無機イオン交換体)
- 配向性透明酸化亜鉛の二光子吸収係数の測定
- ケイ酸塩ガラスを用いたサファイア単結晶とアルミナとの接合
- チタン酸バリウムへのLa_2O_3の固溶
- セラミックスを研究する大学教官の講義への取り組み-日本セラミックス協会教育委員会, 講義に関するアンケートより
- 酸化亜鉛の配向性制御と光学的機能
- 酸化亜鉛バリスターにおけるコバルトの添加効果
- 調製条件の異なるチタン酸バリウム厚膜における機械強度・絶縁強度分布の相関(セラミックレターズ)
- p-n半導体コンタクトを用いたアルコールセンサ
- p-n半導体コンタクトによる分子認識
- 岡崎清先生と電子材料セラミックス
- 調理用電子レンジで焼結した部分安定化ジルコニアの微細構造と強度