電解重合ポリアニリン膜の作成とエレクトロ・クロミック(EC)特性

スポンサーリンク

概要

• 論文の詳細を見る

• The poly-Aniline films was made by the electro-polymerization with five kinds electrolytes components(I〜V) on the glass having the NESA conductive electrode. In the result, the relation of the poly-Aniline polymerization total charge and the polymerization voltage rising speed (voltage is rose from 0[V] to 2[V], rising speed (1〜30 [mV/s]) is know clearly, and this relation have 3 types. The poly-Aniline films be made in the electrolyte componentes (I and IV, V) show the electro -cromic phenomenon (EC) in the supporting electrolyte HCl, H_2SO_4 having the NESA or Pt electrode. When the Pt electrode, the EC is occur lower voltage than the NESA electrode. In this paper, the relation between the EC transmittance spectrum and the applied voltage is described. But, the polymerization films be made in the electrolyte components (II and III) is not occur EC characteristic, however, this film have the expected electro-motive force characteristic, and this characteristic will be reported in other paper.

• 福山大学の論文

著者

• 飯田 義直

  福山大学工学部電子・電気工学科

• 藤村 浩一

  福山大学工学部工学研究科

関連論文

• アニリン電解重合のボルタモグラムおよび重合膜のECにおける電流特性
• 支持電解液を含浸したPVA層を有するポリアニリンのエレクトロクロミック素子の特性
• 支持電解液を含浸したPVA層を有するポリアニリンのエレクトロクロミック素子の特性
• 染色フィルターを有するa-Si色彩センサーの基礎的研究および応用
• 電解重合ポリアニリン膜の作成とエレクトロ・クロミック(EC)特性

スポンサーリンク