Photoluminescent properties of fresnoite phosphors prepared from phase-separated BaO-TiO_2-SiO_2 glasses
スポンサーリンク
概要
- 論文の詳細を見る
Glass ceramic phosphors containing fresnoite (Ba_2TiSi_2O_8) were prepared from glasses both within and outside the immiscibility region of the BaO-TiO_2-SiO_2 system by conventional melt-quenching and subsequent heat treatment. The phosphors showed blue-white photoluminescence (PL) under ultraviolet excitation, and the effects of the crystalline phase precipitated and the fine structure of the ceramics on their PL properties were examined. Phase-separated textures were observed in the samples with compositions within the immiscibility region. The predominant crystalline phase precipitated in the heat-treated sample was fresnoite. Sample PL intensity was related not only to the amount of precipitated fresnoite, but also to the microstructure of the sample resulting from phase separation. The highest PL intensity was obtained from a 22BaO・11TiO_2・67SiO_2 sample from the immiscibility region, because of the formation of an appropriate fine glass-ceramic structure for photo-excitation of fresnoite.
- 社団法人日本セラミックス協会の論文
- 2008-12-01
著者
-
KISHI Tetsuo
Department of Materials Science and Technology, Faculty of Industrial Science and Technology, Tokyo
-
YASUMORI Atsuo
Department of Materials Science and Technology, Faculty of Industrial Science and Technology, Tokyo
-
Yasumori Atsuo
Department Of Materials Science And Technology Tokyo University Of Science
-
Kishi Tetsuo
Department Of Materials Science And Technology Tokyo University Of Science
-
Yasumori Atsuo
Department Of Materials Science And Technology Faculty Of Industrial Science And Technology Tokyo Un
-
HIJIYA Hiroyuki
Department of Materials Science and Technology, Tokyo University of Science
-
Kishi Tetsuo
Department Of Materials Science And Technology Faculty Of Industrial Science And Technology Tokyo Un
-
Hijiya Hiroyuki
Department Of Materials Science And Technology Tokyo University Of Science
関連論文
- Photocatalytic machining of organic molecular layer on a Si wafer surface by use of a porous TiO_2 micro wire
- FAST FORMATION OF ZSM-5 ZEOLITE USING MICROPOROUS SILICA OBTAINED FROM SELECTIVE LEACHING OF METAKAOLINITE
- XPS and X-ray AES(XAES) Study of Various Aluminate Compounds (第19回表面科学講演大会論文特集(2))
- CHARACTERIZATION OF MICROPOROUS SILICA PREPARED BY SELECTIVE LEACHING OF CALCINED KAOLINITE : EFFECT OF CALCINING TEMPERATURE
- Effect of phase separation on crystallization of glasses in the BaO-TiO_2-SiO_2 system
- Photoluminescent properties of fresnoite phosphors prepared from phase-separated BaO-TiO_2-SiO_2 glasses
- THERMAL CHANGE OF HYDROTALCITE-TYPE LAYERED DOUBLE HYDROXIDE Al_2Li(OH)_6[Fe(CN)_6]_・nH_2O UNDER OXIDIZING AND REDUCING ATMOSPHERES
- Preparation and Molecular Recognition of SERS Probe Based on Gold Nanoparticles Constructed from PEG-Oligoamine Copolymer Possessing a Coumarin Group between PEG and Oligoamine
- ADSORPTION PROPERTIES OF MICROPOROUS SILICA PREPARED FROM METAKAOLINITE BY SELECTIVE LEACHING METHOD