Static Debonding Initiation Stress of Fiber Glass Composite
スポンサーリンク
概要
- 論文の詳細を見る
Mesoscale debonding initiation stress of a bundle of glass fibers and epoxy matrix under static loading is investigated. A special cylindrical bar specimen was designed for the experiment. The specimen contains a bundle of glass fibers in the center and the bundle diameters were 1 and 2mm. The fiber diameter is 7μm. A static tension test was performed under the displacement control. The applied load-displacement curve was recorded for each specimen and then the debonding initiation load was defined as the deviation point from the linear curve. In addition, the debonding length was measured directly from the tested specimen. Using the debonding load measured from experiment, an axisymmetric finite element analysis is performed and debonding parameters K_1 and K_2 were computed. The results show the debonding initiation is fully dominated by an opening mode rather than a sliding mode and the stress intensity factor K_1 for the debonding initiation is 2.0E+05 Pa√<m>. The mixed mode fracture takes place in the debonding propagation with constant mode mixity around 41.0 degree and the averaged stress intensity factors are 1.67E+05 Pa√<m> and 1.41E+05 Pa√<m> for the opening and the sliding mode, respectively.
- 一般社団法人日本機械学会の論文
- 2004-04-15
著者
-
Gunawan F
Toyohashi Univ. Technol.
-
Homma Hiroomi
International Cooperation Center For Engineering Education Development Toyohashi University Of Techn
-
Homma Hiroomi
International Cooperation Center For Engineering Education Development Toyohashi University Of Techn
-
Yamauchi Motoharu
Dainippon Screen Mfg. Co. Ltd.
-
Gunawan Fergyanto
Department Of Mechanical Engineering Toyohashi University Of Technology
-
KURNIAWATI Fenny
Light-weight Structure and Aerodynamic Laboratory, Bandung Institute of Technology
-
Kurniawati Fenny
Light-weight Structure And Aerodynamic Laboratory Bandung Institute Of Technology
-
HOMMA Hiroomi
International Cooperation Center for Engineering Education Development
関連論文
- 若手技術者育成が目指すもの
- Numerical Analysis of Kidney Stone Fragmentation by Short Pulse Impingement
- 破壊靱性に対する材料非均質性の影響 : 温度勾配の影響
- 国際インターンシップについて
- 延性-脆性遷移領域における破壊靱性の予測
- 国際化に向けた出版事業
- インドネシア工学系高等教育界に与えたHEDSプロジェクトのインパクト (大学と国際教育協力)
- Accreditation System in Indonesia(JSME NEWS)
- 809 DYNAMIC DEBONDING STRENGTH OF FIBER GLASS COMPOSITE
- Efficient Iterative Solution for Large Elasto-Dynamic Inverse Problems
- Estimation of Dynamic Stress Intensity for One-Point Bend Specimen by Inverse Analysis(Fracture Mechanics)
- 141 INVERSE ANALYSIS ON IMPACT OF ONE-POINT BEND SPECIMEN
- Static Debonding Initiation Stress of Fiber Glass Composite
- Estimation of Dynamic Stress Intensity for One-Point Bend Specimen by Inverse Analysis(Fracture Mechanics)
- Nugget Strength of Spot Weld under Shear Impact Load