Neutron Irradiation Effects of V-Ti Binary Alloys

スポンサーリンク

概要

• 論文の詳細を見る

• Mechanical Properties and microstructures of four kinds of V-Ti binary alloys were examined before and after neutron irradiation. The neutron irradiation was done in JMTR (Japan Material Testing Reactor) at an ambient temperature up to 1.5xl0^<23> n/m^2 (E>0.1MeV) and in RTNS-II (Rotating Target Neutron Source-II) at room temperature up to 5x10^<22>n/m^2 (14MeV). The tensile yield strength of unirradiated V-Ti alloys increased with Ti contents, it indicated a maximum value at near V-40Ti and slightly decreased at V-60Ti. The yield strength of high Ti contents V alloys were slightly affected by neutron irradiations. JMTR irradiation gave many effects on the tensile property, while RTNS-II irradiation affected only the elongation.

• 東北大学の論文
• 1991-03-05

著者

• Iseki Michio

  Department of Nuclear Engineering, Faculty of Engineering, Nagoya University

• Iseki M

  Nagoya Univ. Aichi Jpn

• Iseki Michio

  Department Of Nuclear Engineering Faculty Of Engineering Nagoya University

関連論文

• Trapping and detrapping of hydrogen in graphite materials exposed to hydrogen gas
• Neutron Irradiation Effects of V-Ti Binary Alloys
• PROPOSAL FOR FFTF MOTA EXPERIMENTS ON CERAMICS AND COMPOSITE MATERIALS : SUB-GROUP (E) PROGRAM

スポンサーリンク