Microstructure, Mechanical Properties and Fracture Behavior of α Particle Irradiated Type 316 Stainless Steel

概要

論文の詳細を見る
The present work is a research of the effect of helium on the microstructure, mechanical properties and fracture behaviors of a type 316 austenitic steel. Helium implantation was performed by 30-MeV α-particle injection on very small size specimens, using a cyclotron. Average helium content in a He-deposited region was up to 2000 appm He. In the case of 2000appm He implantation, intergranular fracture was sometimes observed on the helium deposited region after tensile test at room temperature. At elevated temperature test, however, this material showed the transition of fracture mode from transgranular-ductile fracture at 773K to intergranular fracture at 873. In the case of 500 appm He implantation, the transition of fracture mode was recognized at a temperature range of 873K to 973K.
東北大学の論文
1991-03-05