Effects of Growth Rates and Cooling Rates on Defect Generation in Melt-Grown Copper Crystals(Physics)
スポンサーリンク
概要
- 論文の詳細を見る
Single crystals of zone-refined Cu were grown from the melt at growth rates ranging from 0.1 to 29.0 mm/min and with cooling rates of the crystal after growth varying from 0.24 to 45℃/min. It was found that the growth rate had a very important effect on the generation of dislocations and their arrays, but the cooling rate of the crystal after growth had an important effect only when the crystal had been solidified at a rate of 0.1 mm/min.